Crastin® T843FR BK851

Alternative and trade names
PBTC-GF20FR(17)
Want to keep this datasheet? Save it now in your required format

Description

Crastin® T843FR BK851 is a 20% Glass Reinforced, Flame Retardant, Toughened, Polybutylene Terephthalate

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.59 g/cm³

Show Material materials with Density of 1.59 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

5.8 GPa

Show Material materials with Elastic modulus of 5.8 GPa

ISO 527-1/-2

Elongation

23.0 °C

4 %

Show Material materials with Elongation of 4 %

ISO 527-1/-2

Flexural strength

23.0 °C

142 MPa

Show Material materials with Flexural strength of 142 MPa

ISO 178

Impact strength, Charpy notched

23.0 °C

9 kJ/m²

Show Material materials with Impact strength, Charpy notched of 9 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

23.0 °C

55 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 55 kJ/m²

ISO 179/1eU

Impact strength, Izod unnotched

23.0 °C

8 kJ/m²

Show Material materials with Impact strength, Izod unnotched of 8 kJ/m²

ISO 180/1A

Poisson's ratio

23.0 °C

0.35 [-]

Show Material materials with Poisson's ratio of 0.35 [-]

Tensile strength

23.0 °C

87 MPa

Show Material materials with Tensile strength of 87 MPa

ISO 527-1/-2

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

180 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 180 °C

ISO 75-1/-2

Melting point

205 °C

Show Material materials with Melting point of 205 °C

ISO 11357-1/-3 | 18°F/min

Relative temperature index, electrical

130 °C

Show Material materials with Relative temperature index, electrical of 130 °C

UL 746B | 240mil

Relative temperature index, mechanical impact

130 °C

Show Material materials with Relative temperature index, mechanical impact of 130 °C

UL 746B | 240mil

Relative temperature index, mechanical strength

130 °C

Show Material materials with Relative temperature index, mechanical strength of 130 °C

UL 746B | 240mil

Flammability

Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 3 mm, UL recognition: yes -, Oxygen index: 31 %, Glow Wire Flammability Index, 120mil: 960 °C, FMVSS Class: DNI -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

225 V

Show Material materials with Comparative tracking index of 225 V

IEC 60112

Dielectric constant, 100Hz

23.0 °C

5.2 [-]

Show Material materials with Dielectric constant, 100Hz of 5.2 [-]

IEC 62631-2-1

Dielectric constant, 1MHz

23.0 °C

4.7 [-]

Show Material materials with Dielectric constant, 1MHz of 4.7 [-]

IEC 62631-2-1

Dissipation factor, 100Hz

23.0 °C

0.02 [-]

Show Material materials with Dissipation factor, 100Hz of 0.02 [-]

IEC 62631-2-1

Dissipation factor, 1MHz

23.0 °C

0.03 [-]

Show Material materials with Dissipation factor, 1MHz of 0.03 [-]

IEC 62631-2-1

Surface resistivity

23.0 °C

1.00E+14 Ω/sq

Show Material materials with Surface resistivity of 1.00E+14 Ω/sq

IEC 62631-3-2

Volume resistivity

23.0 °C

1.00E+15 Ω·cm

Show Material materials with Volume resistivity of 1.00E+15 Ω·cm

min. | IEC 62631-3-1

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.5 %

Show Material materials with Shrinkage of 0.5 %

ISO 294-4, 2577

Shrinkage, transverse

23.0 °C

1.1 %

Show Material materials with Shrinkage, transverse of 1.1 %

ISO 294-4, 2577

Technological properties

Property
Fillers

20% Glass Fiber

Processing methods

Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 150°C