Delrin® 300TE NC010

Alternative and trade names
POM-I
Want to keep this datasheet? Save it now in your required format

Description

Common features of Delrin® acetal resins include mechanical and physical properties such as high mechanical strength and rigidity, excellent fatigue and impact resistance, as well as resistance to moisture, gasoline, lubricants, solvents, and many other neutral chemicals. Delrin® acetal resins also have excellent dimensional stability and good electrical insulating characteristics. They are naturally resilient, self-lubricating, and available in a variety of colors and speciality grades. Delrin® acetal resin typically is used in demanding applications in the automotive, domestic appliances, sports, industrial engineering, electronics, and consumer goods industries.Delrin® 300TE is a toughened medium-high viscosity acetal homopolymer for injection molding with very low VOC emissions for applications in automotive interiors.

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.38 g/cm³

Show Material materials with Density of 1.38 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

1.9 GPa

Show Material materials with Elastic modulus of 1.9 GPa

ISO 527-1/-2

Elongation

23.0 °C

36 %

Show Material materials with Elongation of 36 %

ISO 527-1/-2 | 50mm/min

Elongation at yield

23.0 °C

20 %

Show Material materials with Elongation at yield of 20 %

ISO 527-1/-2

Flexural modulus

23.0 °C

1.9 GPa

Show Material materials with Flexural modulus of 1.9 GPa

ISO 178

Hardness, Rockwell M

23.0 °C

69.3 [-]

Show Material materials with Hardness, Rockwell M of 69.3 [-]

ISO 2039-2

Hardness, Rockwell R

23.0 °C

116 [-]

Show Material materials with Hardness, Rockwell R of 116 [-]

ISO 2039-2

Impact strength, Charpy notched

-6.0 °C

10 kJ/m²

Show Material materials with Impact strength, Charpy notched of 10 kJ/m²

ISO 179/1eA

Poisson's ratio

23.0 °C

0.41 [-]

Show Material materials with Poisson's ratio of 0.41 [-]

Yield strength

23.0 °C

53 MPa

Show Material materials with Yield strength of 53 MPa

ISO 527-1/-2

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

1.2E-4 1/K

Show Material materials with Coefficient of thermal expansion of 1.2E-4 1/K

ISO 11359-1/-2

Coefficient of thermal expansion, transverse

23.0 °C

1.3E-4 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 1.3E-4 1/K

ISO 11359-1/-2

Heat deflection temperature, 0.45 MPa

132 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 132 °C

ISO 75-1/-2

Heat deflection temperature, 1.80 MPa

71 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 71 °C

ISO 75-1/-2

Melting point

178 °C

Show Material materials with Melting point of 178 °C

ISO 11357-1/-3 | 18°F/min

Specific heat capacity

23.0 °C

2880 J/(kg·K)

Show Material materials with Specific heat capacity of 2880 J/(kg·K)

of melt

Vicat softening temperature

172 °C

Show Material materials with Vicat softening temperature of 172 °C

ISO 306 | 90°F, 2 lbf

Flammability

FMVSS Class: B -, Burning rate, Thickness 1 mm: 46 mm/min

Rheological Properties

PropertyTemperatureValueComment

Melt mass-flow rate

6 g/10min

Show Material materials with Melt mass-flow rate of 6 g/10min

ISO 1133 | 190°C/2.16kg

Shrinkage

23.0 °C

1.3 %

Show Material materials with Shrinkage of 1.3 %

ISO 294-4, 2577

Shrinkage, transverse

23.0 °C

1.5 %

Show Material materials with Shrinkage, transverse of 1.5 %

ISO 294-4, 2577

Technological properties

Property
Processing methods

Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 4-8h, Processing Moisture Content: ≤0.05%, Melt Temperature Optimum: 205°C, Min. melt temperature: 200°C, Max. melt temperature: 210°C, Mold Temperature Optimum: 50°C, Min. mold temperature: 40°C, Max. mold temperature: 60°C, Hold pressure range: 60-80MPa, Hold pressure time: 7.5s/mm, Ejection temperature: 115°C