General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.71 g/cm³ Show Material materials with Density of 1.71 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.3 % Show Material materials with Water absorption of 0.3 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 11 GPa Show Material materials with Elastic modulus of 11 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2.4 % Show Material materials with Elongation of 2.4 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 9.5 GPa Show Material materials with Flexural modulus of 9.5 GPa | ISO 178 |
Flexural strength | 23.0 °C | 215 MPa Show Material materials with Flexural strength of 215 MPa | ISO 178 |
Impact strength, Charpy notched | -6.0 °C | 9 kJ/m² Show Material materials with Impact strength, Charpy notched of 9 kJ/m² | ISO 179/1eA |
23.0 °C | 9 kJ/m² Show Material materials with Impact strength, Charpy notched of 9 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 55 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 55 kJ/m² | ISO 179/1eU |
23.0 °C | 55 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 55 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | -30.0 °C | 40 kJ/m² Show Material materials with Impact strength, Izod notched of 40 kJ/m² | ISO 180/1U |
23.0 °C | 40 kJ/m² Show Material materials with Impact strength, Izod notched of 40 kJ/m² | ISO 180/1U | |
Impact strength, Izod unnotched | -30.0 °C | 8 kJ/m² Show Material materials with Impact strength, Izod unnotched of 8 kJ/m² | ISO 180/1A |
23.0 °C | 9 kJ/m² Show Material materials with Impact strength, Izod unnotched of 9 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 120 MPa Show Material materials with Tensile strength of 120 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 3E-5 1/K Show Material materials with Coefficient of thermal expansion of 3E-5 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 9E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 9E-5 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 220 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 220 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 210 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 210 °C | ISO 75-1/-2 | |||
Melting point | 225 °C Show Material materials with Melting point of 225 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 240mil | |||
Specific heat capacity | 23.0 °C | 1600 J/(kg·K) Show Material materials with Specific heat capacity of 1600 J/(kg·K) | of melt | ||
Vicat softening temperature | 212 °C Show Material materials with Vicat softening temperature of 212 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 0.75 mm, UL recognition: yes -, Oxygen index: 31 %, Glow Wire Flammability Index, 15mil: 960 °C, Glow Wire Flammability Index, 30mil: 960 °C, Glow Wire Flammability Index, 40mil: 960 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 80mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 675 °C, Glow Wire Ignition Temperature, 15mil: 675 °C, Glow Wire Ignition Temperature, 40mil: 675 °C, Glow Wire Ignition Temperature, 60mil: 675 °C, Glow Wire Ignition Temperature, 120mil: 775 °C, Glow Wire Temperature, No Flame, 40mil: 650 °C, FMVSS Class: DNI -, Railway classification: R23 -, Railway classification rating: HL1 - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 250 V Show Material materials with Comparative tracking index of 250 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 4.5 [-] Show Material materials with Dielectric constant, 100Hz of 4.5 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 3.8 [-] Show Material materials with Dielectric constant, 1MHz of 3.8 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 17 kV/mm Show Material materials with Dielectric strength of 17 kV/mm | IEC 60243-1 | Short Time, 2mm |
Dissipation factor, 100Hz | 23.0 °C | 3E-3 [-] Show Material materials with Dissipation factor, 100Hz of 3E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Surface resistivity | 23.0 °C | 1.00E+15 Ω/sq Show Material materials with Surface resistivity of 1.00E+15 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 9 g/10min Show Material materials with Melt mass-flow rate of 9 g/10min | ISO 1133 | 250°C/5kg | |
Melt volume-flow rate | 11 cm³/10min Show Material materials with Melt volume-flow rate of 11 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 0.5 % Show Material materials with Shrinkage of 0.5 % | ISO 294-4 | Annealed |
Shrinkage, transverse | 23.0 °C | 1.5 % Show Material materials with Shrinkage, transverse of 1.5 % | ISO 294-4 | Annealed |
Technological properties
Property | ||
---|---|---|
Fillers | 30% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |