General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.37 g/cm³ Show Material materials with Density of 1.37 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 1.9 GPa Show Material materials with Elastic modulus of 1.9 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 500 % Show Material materials with Elongation of 500 % | min. | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 25 % Show Material materials with Elongation at yield of 25 % | ISO 527-1/-2 | ||
Flexural modulus | 23.0 °C | 1.85 GPa Show Material materials with Flexural modulus of 1.85 GPa | ISO 178 | ||
Hardness, Rockwell M | 23.0 °C | 64.6 [-] Show Material materials with Hardness, Rockwell M of 64.6 [-] | ISO 2039-2 | ||
Hardness, Rockwell R | 23.0 °C | 113 [-] Show Material materials with Hardness, Rockwell R of 113 [-] | ISO 2039-2 | ||
Impact strength, Charpy notched | -6.0 °C | 14 kJ/m² Show Material materials with Impact strength, Charpy notched of 14 kJ/m² | ISO 179/1eA | ||
23.0 °C | 25 kJ/m² Show Material materials with Impact strength, Charpy notched of 25 kJ/m² | ISO 179/1eA | |||
Poisson's ratio | 23.0 °C | 0.41 [-] Show Material materials with Poisson's ratio of 0.41 [-] | |||
Yield strength | 23.0 °C | 54 MPa Show Material materials with Yield strength of 54 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy unnotched | No Break @ 23,-6°C, ISO 179/1eA |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.2E-4 1/K Show Material materials with Coefficient of thermal expansion of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.2E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 126 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 126 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 71 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 71 °C | ISO 75-1/-2 | |||
Melting point | 178 °C Show Material materials with Melting point of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
Vicat softening temperature | 173 °C Show Material materials with Vicat softening temperature of 173 °C | ISO 306 | 90°F, 2 lbf | |||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: 42 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 2.2 g/10min Show Material materials with Melt mass-flow rate of 2.2 g/10min | ISO 1133 | 190°C/2.16kg | |
Melt volume-flow rate | 2 cm³/10min Show Material materials with Melt volume-flow rate of 2 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 1.3 % Show Material materials with Shrinkage of 1.3 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.5 % Show Material materials with Shrinkage, transverse of 1.5 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 4-8h, Processing Moisture Content: ≤0.05%, Melt Temperature Optimum: 205°C, Min. melt temperature: 200°C, Max. melt temperature: 210°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 50°C, Min. mold temperature: 40°C, Max. mold temperature: 60°C, Hold pressure range: 60-80MPa, Hold pressure time: 7.5s/mm |