General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.41 g/cm³ Show Material materials with Density of 1.41 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2.3 GPa Show Material materials with Elastic modulus of 2.3 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 16 % Show Material materials with Elongation of 16 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 2.1 GPa Show Material materials with Flexural modulus of 2.1 GPa | ISO 178 |
Flexural strength | 23.0 °C | 57 MPa Show Material materials with Flexural strength of 57 MPa | ISO 178 |
Hardness, Rockwell M | 23.0 °C | 75 [-] Show Material materials with Hardness, Rockwell M of 75 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -6.0 °C | 6 kJ/m² Show Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO 179/1eA |
23.0 °C | 8 kJ/m² Show Material materials with Impact strength, Charpy notched of 8 kJ/m² | ISO 179/1eA | |
Impact strength, Izod unnotched | 23.0 °C | 7 kJ/m² Show Material materials with Impact strength, Izod unnotched of 7 kJ/m² | ISO 180/1A |
Poisson's ratio | 23.0 °C | 0.39 [-] Show Material materials with Poisson's ratio of 0.39 [-] | |
Tensile strength | 23.0 °C | 50 MPa Show Material materials with Tensile strength of 50 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.2E-4 1/K Show Material materials with Coefficient of thermal expansion of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.2E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 135 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 135 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 70 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 70 °C | ISO 75-1/-2 | |||
Melting point | 178 °C Show Material materials with Melting point of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Surface resistivity | 23.0 °C | 20000 Ω/sq Show Material materials with Surface resistivity of 20000 Ω/sq | ASTM D 4496 |
Volume resistivity | 23.0 °C | 100000 Ω·cm Show Material materials with Volume resistivity of 100000 Ω·cm | ASTM D 4496 | conductive plastics |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 3 g/10min Show Material materials with Melt mass-flow rate of 3 g/10min | ISO 1133 | 190°C/2.16kg | |
Melt volume-flow rate | 2.3 cm³/10min Show Material materials with Melt volume-flow rate of 2.3 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 1.7 % Show Material materials with Shrinkage of 1.7 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.5 % Show Material materials with Shrinkage, transverse of 1.5 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Fillers | Carbon Black | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.05%, Melt Temperature Optimum: 205°C, Min. melt temperature: 200°C, Max. melt temperature: 210°C, Mold Temperature Optimum: 50°C, Min. mold temperature: 40°C, Max. mold temperature: 60°C, Hold pressure range: 60-80MPa, Hold pressure time: 7.5s/mm |