General
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of friction | 0.2 [-] Show Material materials with Coefficient of friction of 0.2 [-] | ASTM 1894 | 1h against steel | |
Density | 23.0 °C | 1.66 g/cm³ Show Material materials with Density of 1.66 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.3 % Show Material materials with Water absorption of 0.3 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 14.2 GPa Show Material materials with Elastic modulus of 14.2 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2 % Show Material materials with Elongation of 2 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 13.3 GPa Show Material materials with Flexural modulus of 13.3 GPa | ISO 178 |
Flexural strength | 23.0 °C | 210 MPa Show Material materials with Flexural strength of 210 MPa | ISO 178 |
Impact strength, Charpy notched | 23.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA |
Impact strength, Charpy unnotched | -6.0 °C | 65 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 65 kJ/m² | ISO 179/1eU |
23.0 °C | 55 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 55 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | -30.0 °C | 50 kJ/m² Show Material materials with Impact strength, Izod notched of 50 kJ/m² | ISO 180/1U |
Impact strength, Izod unnotched | -30.0 °C | 10 kJ/m² Show Material materials with Impact strength, Izod unnotched of 10 kJ/m² | ISO 180/1A |
23.0 °C | 10 kJ/m² Show Material materials with Impact strength, Izod unnotched of 10 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | |
Tensile strength | 23.0 °C | 140 MPa Show Material materials with Tensile strength of 140 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2E-5 1/K Show Material materials with Coefficient of thermal expansion of 2E-5 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 8E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 8E-5 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 222 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 222 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 207 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 207 °C | ISO 75-1/-2 | |||
Melting point | 225 °C Show Material materials with Melting point of 225 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 125 °C Show Material materials with Relative temperature index, mechanical impact of 125 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | 120mil | |||
Vicat softening temperature | 215 °C Show Material materials with Vicat softening temperature of 215 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Oxygen index: 20 %, Glow Wire Flammability Index, 120mil: 750 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 475 V Show Material materials with Comparative tracking index of 475 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 4.1 [-] Show Material materials with Dielectric constant, 100Hz of 4.1 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 3.9 [-] Show Material materials with Dielectric constant, 1MHz of 3.9 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 32 kV/mm Show Material materials with Dielectric strength of 32 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 3.8E-3 [-] Show Material materials with Dissipation factor, 100Hz of 3.8E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 6 g/10min Show Material materials with Melt mass-flow rate of 6 g/10min | ISO 1133 | 250°C/5kg | |
Melt volume-flow rate | 4 cm³/10min Show Material materials with Melt volume-flow rate of 4 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 0.3 % Show Material materials with Shrinkage of 0.3 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.1 % Show Material materials with Shrinkage, transverse of 1.1 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Fillers | 45% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 260°C, Min. melt temperature: 250°C, Max. melt temperature: 270°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |