General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.53 g/cm³ Show Material materials with Density of 1.53 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.35 % Show Material materials with Water absorption of 0.35 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 10 GPa Show Material materials with Elastic modulus of 10 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2.7 % Show Material materials with Elongation of 2.7 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 9 GPa Show Material materials with Flexural modulus of 9 GPa | ISO 178 |
Flexural strength | 23.0 °C | 200 MPa Show Material materials with Flexural strength of 200 MPa | ISO 178 |
Hardness, Ball Indentation | 23.0 °C | 205 MPa Show Material materials with Hardness, Ball Indentation of 205 MPa | ISO 2039-1 |
Impact strength, Charpy notched | 23.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA |
Impact strength, Charpy unnotched | 23.0 °C | 65 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 65 kJ/m² | ISO 179/1eU |
Impact strength, Izod notched | -40.0 °C | 55 kJ/m² Show Material materials with Impact strength, Izod notched of 55 kJ/m² | ISO 180/1U |
-30.0 °C | 55 kJ/m² Show Material materials with Impact strength, Izod notched of 55 kJ/m² | ISO 180/1U | |
23.0 °C | 60 kJ/m² Show Material materials with Impact strength, Izod notched of 60 kJ/m² | ISO 180/1U | |
Impact strength, Izod unnotched | 23.0 °C | 9 kJ/m² Show Material materials with Impact strength, Izod unnotched of 9 kJ/m² | ISO 180/1A |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 140 MPa Show Material materials with Tensile strength of 140 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 205 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 205 °C | ISO 75-1/-2 | |||
Melting point | 225 °C Show Material materials with Melting point of 225 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | 240mil | |||
Specific heat capacity | 23.0 °C | 1730 J/(kg·K) Show Material materials with Specific heat capacity of 1730 J/(kg·K) | of melt | ||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Oxygen index: 20 %, Glow Wire Flammability Index, 30mil: 725 °C, Glow Wire Flammability Index, 60mil: 725 °C, Glow Wire Flammability Index, 120mil: 750 °C, Glow Wire Ignition Temperature, 30mil: 750 °C, Glow Wire Ignition Temperature, 60mil: 750 °C, Glow Wire Ignition Temperature, 120mil: 775 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 54 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 225 V Show Material materials with Comparative tracking index of 225 V | IEC 60112 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 10 g/10min Show Material materials with Melt mass-flow rate of 10 g/10min | ISO 1133 | 250°C/2.16kg | |
Melt volume-flow rate | 7 cm³/10min Show Material materials with Melt volume-flow rate of 7 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 0.3 % Show Material materials with Shrinkage of 0.3 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.1 % Show Material materials with Shrinkage, transverse of 1.1 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Fillers | 30% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |