General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.43 g/cm³ Show Material materials with Density of 1.43 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 3 GPa Show Material materials with Elastic modulus of 3 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 35 % Show Material materials with Elongation of 35 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 25 % Show Material materials with Elongation at yield of 25 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 2.8 GPa Show Material materials with Flexural modulus of 2.8 GPa | ISO 178 |
Impact strength, Charpy notched | -6.0 °C | 8 kJ/m² Show Material materials with Impact strength, Charpy notched of 8 kJ/m² | ISO 179/1eA |
23.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | 23.0 °C | 150 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 150 kJ/m² | ISO 179/1eU |
Poisson's ratio | 23.0 °C | 0.37 [-] Show Material materials with Poisson's ratio of 0.37 [-] | |
Yield strength | 23.0 °C | 71 MPa Show Material materials with Yield strength of 71 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.1E-4 1/K Show Material materials with Coefficient of thermal expansion of 1.1E-4 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.1E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.1E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 158 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 158 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 95 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 95 °C | ISO 75-1/-2 | |||
Melting point | 178 °C Show Material materials with Melting point of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: 42 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 2.2 g/10min Show Material materials with Melt mass-flow rate of 2.2 g/10min | ISO 1133 | 190°C/2.16kg | |
Shrinkage | 23.0 °C | 1.8 % Show Material materials with Shrinkage of 1.8 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.7 % Show Material materials with Shrinkage, transverse of 1.7 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Fillers | 1.5% PTFE | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 215°C, Min. melt temperature: 210°C, Max. melt temperature: 220°C, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 90-110MPa, Hold pressure time: 8s/mm |