General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.41 g/cm³ Show Material materials with Density of 1.41 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 3.1 GPa Show Material materials with Elastic modulus of 3.1 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 15 % Show Material materials with Elongation of 15 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 3 GPa Show Material materials with Flexural modulus of 3 GPa | ISO 178 |
Impact strength, Charpy notched | -6.0 °C | 3.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 3.5 kJ/m² | ISO 179/1eA |
23.0 °C | 4.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 4.5 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 60 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 60 kJ/m² | ISO 179/1eU |
23.0 °C | 50 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 50 kJ/m² | ISO 179/1eU | |
Poisson's ratio | 23.0 °C | 0.37 [-] Show Material materials with Poisson's ratio of 0.37 [-] | |
Tensile strength | 23.0 °C | 65 MPa Show Material materials with Tensile strength of 65 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 9.4E-5 1/K Show Material materials with Coefficient of thermal expansion of 9.4E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 9.2E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 9.2E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Heat deflection temperature, 0.45 MPa | 160 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 160 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 98 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 98 °C | ISO 75-1/-2 | |||
Melting point | 178 °C Show Material materials with Melting point of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: 34 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 2 g/10min Show Material materials with Melt mass-flow rate of 2 g/10min | ISO 1133 | 190°C/2.16kg | |
Melt volume-flow rate | 1.7 cm³/10min Show Material materials with Melt volume-flow rate of 1.7 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 1.8 % Show Material materials with Shrinkage of 1.8 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.5 % Show Material materials with Shrinkage, transverse of 1.5 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Fillers | Aramid Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 215°C, Min. melt temperature: 210°C, Max. melt temperature: 220°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 90-110MPa, Hold pressure time: 8s/mm |