General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.54 g/cm³ Show Material materials with Density of 1.54 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.35 % Show Material materials with Water absorption of 0.35 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 3.9 GPa Show Material materials with Elastic modulus of 3.9 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 4.7 % Show Material materials with Elongation of 4.7 % | ISO 527-1/-2 |
Impact strength, Charpy notched | -6.0 °C | 5 kJ/m² Show Material materials with Impact strength, Charpy notched of 5 kJ/m² | ISO 179/1eA |
23.0 °C | 8.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 8.5 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 40 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 40 kJ/m² | ISO 179/1eU |
23.0 °C | 46 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 46 kJ/m² | ISO 179/1eU | |
Poisson's ratio | 23.0 °C | 0.36 [-] Show Material materials with Poisson's ratio of 0.36 [-] | |
Tensile strength | 23.0 °C | 70 MPa Show Material materials with Tensile strength of 70 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 170 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 170 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 8.0 MPa | 66 °C Show Material materials with Heat deflection temperature, 8.0 MPa of 66 °C | ISO 75-1/-2 | |||
Melting point | 205 °C Show Material materials with Melting point of 205 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | 240mil | |||
Specific heat capacity | 23.0 °C | 1970 J/(kg·K) Show Material materials with Specific heat capacity of 1970 J/(kg·K) | of melt | ||
Vicat softening temperature | 180 °C Show Material materials with Vicat softening temperature of 180 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 0.75 mm, UL recognition: yes -, Oxygen index: 30 %, Glow Wire Flammability Index, 120mil: 960 °C, FMVSS Class: DNI - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 250 V Show Material materials with Comparative tracking index of 250 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 4 [-] Show Material materials with Dielectric constant, 100Hz of 4 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 3.8 [-] Show Material materials with Dielectric constant, 1MHz of 3.8 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 16 kV/mm Show Material materials with Dielectric strength of 16 kV/mm | IEC 60243-1 | Short Time, 2mm |
Dissipation factor, 100Hz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 100Hz of 0.01 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Material materials with Surface resistivity of 1.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt viscosity | 250.0 °C | 240 Pa·s Show Material materials with Melt viscosity of 240 Pa·s | ISO 11443 | @ 1000 sec-1, 250°C |
Shrinkage | 23.0 °C | 0.7 % Show Material materials with Shrinkage of 0.7 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.2 % Show Material materials with Shrinkage, transverse of 1.2 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Fillers | 10% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 110°C, Min. mold temperature: 100°C, Max. mold temperature: 120°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 150°C |