General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.42 g/cm³ Show Material materials with Density of 1.42 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.9 % Show Material materials with Water absorption of 0.9 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 3.4 GPa Show Material materials with Elastic modulus of 3.4 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 20 % Show Material materials with Elongation of 20 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 12 % Show Material materials with Elongation at yield of 12 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 3.2 GPa Show Material materials with Flexural modulus of 3.2 GPa | ISO 178 |
Impact strength, Charpy notched | -6.0 °C | 6 kJ/m² Show Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO 179/1eA |
23.0 °C | 6.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 6.5 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 160 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 160 kJ/m² | ISO 179/1eU |
23.0 °C | 160 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 160 kJ/m² | ISO 179/1eU | |
Poisson's ratio | 23.0 °C | 0.37 [-] Show Material materials with Poisson's ratio of 0.37 [-] | |
Yield strength | 23.0 °C | 74 MPa Show Material materials with Yield strength of 74 MPa | ISO 527-1/-2 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 163 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 163 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 105 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 105 °C | ISO 75-1/-2 | |
Melting point | 178 °C Show Material materials with Melting point of 178 °C | ISO 11357-1/-3 | 18°F/min | |
Relative temperature index, electrical | 110 °C Show Material materials with Relative temperature index, electrical of 110 °C | UL 746B | 120mil | |
Relative temperature index, mechanical impact | 90 °C Show Material materials with Relative temperature index, mechanical impact of 90 °C | UL 746B | 120mil | |
Relative temperature index, mechanical strength | 95 °C Show Material materials with Relative temperature index, mechanical strength of 95 °C | UL 746B | 120mil | |
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.8 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt volume-flow rate | 13 cm³/10min Show Material materials with Melt volume-flow rate of 13 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 1.9 % Show Material materials with Shrinkage of 1.9 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.8 % Show Material materials with Shrinkage, transverse of 1.8 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 215°C, Min. melt temperature: 210°C, Max. melt temperature: 220°C, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 80-100MPa, Hold pressure time: 7.5s/mm |