Description

Crastin® SC193 NC010 (Complete Data) is a 30% Glass Reinforced Polybutylene Terephthalate Blend Developed for Healthcare Industry

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.44 g/cm³

Show Material materials with Density of 1.44 g/cm³

ISO 1183

Water absorption

23.0 °C

0.7 %

Show Material materials with Water absorption of 0.7 %

Sim. to ISO 62 | 80mil

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

9.5 GPa

Show Material materials with Elastic modulus of 9.5 GPa

ISO 527-1/-2

Elongation

23.0 °C

2.5 %

Show Material materials with Elongation of 2.5 %

ISO 527-1/-2

Impact strength, Charpy notched

-6.0 °C

9 kJ/m²

Show Material materials with Impact strength, Charpy notched of 9 kJ/m²

ISO 179/1eA

23.0 °C

10 kJ/m²

Show Material materials with Impact strength, Charpy notched of 10 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

-6.0 °C

66 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 66 kJ/m²

ISO 179/1eU

23.0 °C

60 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 60 kJ/m²

ISO 179/1eU

Unlock all property charts

Poisson's ratio

23.0 °C

0.34 [-]

Show Material materials with Poisson's ratio of 0.34 [-]

Tensile strength

23.0 °C

130 MPa

Show Material materials with Tensile strength of 130 MPa

ISO 527-1/-2

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

2.5E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.5E-5 1/K

ISO 11359-1/-2

Coefficient of thermal expansion, transverse

23.0 °C

1E-4 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 1E-4 1/K

ISO 11359-1/-2

Glass transition temperature

120 °C

Show Material materials with Glass transition temperature of 120 °C

ISO 11357-1/-2 | 18°F/min

Heat deflection temperature, 1.80 MPa

180 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 180 °C

ISO 75-1/-2

Heat deflection temperature, 8.0 MPa

97 °C

Show Material materials with Heat deflection temperature, 8.0 MPa of 97 °C

ISO 75-1/-2

Melting point

225 °C

Show Material materials with Melting point of 225 °C

ISO 11357-1/-3 | 18°F/min

Specific heat capacity

23.0 °C

1900 J/(kg·K)

Show Material materials with Specific heat capacity of 1900 J/(kg·K)

of melt

Vicat softening temperature

150 °C

Show Material materials with Vicat softening temperature of 150 °C

ISO 306 | 90°F/h, 11 lbf

Flammability

Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, Burning Behav. at thickness h: HB class, Thickness tested: 6 mm, Oxygen index: 19 %

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

550 V

Show Material materials with Comparative tracking index of 550 V

IEC 60112

Dielectric constant, 100Hz

23.0 °C

3.8 [-]

Show Material materials with Dielectric constant, 100Hz of 3.8 [-]

IEC 62631-2-1

Dielectric constant, 1MHz

23.0 °C

3.6 [-]

Show Material materials with Dielectric constant, 1MHz of 3.6 [-]

IEC 62631-2-1

Dielectric strength

23.0 °C

36 kV/mm

Show Material materials with Dielectric strength of 36 kV/mm

IEC 60243-1

Dissipation factor, 100Hz

23.0 °C

3E-3 [-]

Show Material materials with Dissipation factor, 100Hz of 3E-3 [-]

IEC 62631-2-1

Dissipation factor, 1MHz

23.0 °C

0.02 [-]

Show Material materials with Dissipation factor, 1MHz of 0.02 [-]

IEC 62631-2-1

Surface resistivity

23.0 °C

1.00E+14 Ω/sq

Show Material materials with Surface resistivity of 1.00E+14 Ω/sq

IEC 62631-3-2

Volume resistivity

23.0 °C

1.00E+15 Ω·cm

Show Material materials with Volume resistivity of 1.00E+15 Ω·cm

min. | IEC 62631-3-1

Rheological Properties

PropertyTemperatureValueComment

Melt volume-flow rate

17 cm³/10min

Show Material materials with Melt volume-flow rate of 17 cm³/10min

ISO 1133

Shrinkage

23.0 °C

0.3 %

Show Material materials with Shrinkage of 0.3 %

ISO 294-4, 2577

Shrinkage, transverse

23.0 °C

0.6 %

Show Material materials with Shrinkage, transverse of 0.6 %

ISO 294-4, 2577

Technological properties

Property
Fillers

30% Glass Fiber

Processing methods

Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C