Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 1.42 g/cm³ Show Material materials with Density of 1.42 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.3 % Show Material materials with Water absorption of 0.3 % | Sim. to ISO 62 | Immersion 24h |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 3.4 GPa Show Material materials with Elastic modulus of 3.4 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 25 % Show Material materials with Elongation of 25 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 12 % Show Material materials with Elongation at yield of 12 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 3.2 GPa Show Material materials with Flexural modulus of 3.2 GPa | ISO 178 |
Hardness, Ball Indentation | 23.0 °C | 175 MPa Show Material materials with Hardness, Ball Indentation of 175 MPa | ISO 2039-1 |
Impact strength, Charpy notched | -6.0 °C | 6 kJ/m² Show Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO 179/1eA |
23.0 °C | 6.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 6.5 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 200 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 200 kJ/m² | ISO 179/1eU |
23.0 °C | 220 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 220 kJ/m² | ISO 179/1eU | |
Poisson's ratio | 23.0 °C | 0.37 [-] Show Material materials with Poisson's ratio of 0.37 [-] | |
Yield strength | 23.0 °C | 75 MPa Show Material materials with Yield strength of 75 MPa | ISO 527-1/-2 |
Thermal
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1E-4 1/K Show Material materials with Coefficient of thermal expansion of 1E-4 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.1E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.1E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 163 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 163 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 107 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 107 °C | ISO 75-1/-2 | |||
Melting point | 178 °C Show Material materials with Melting point of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 110 °C Show Material materials with Relative temperature index, electrical of 110 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 90 °C Show Material materials with Relative temperature index, mechanical impact of 90 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 95 °C Show Material materials with Relative temperature index, mechanical strength of 95 °C | UL 746B | 120mil | |||
Vicat softening temperature | 160 °C Show Material materials with Vicat softening temperature of 160 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.8 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: 25 mm/min | ||||
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 3.9 [-] Show Material materials with Dielectric constant, 100Hz of 3.9 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 3.9 [-] Show Material materials with Dielectric constant, 1MHz of 3.9 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 3E-3 [-] Show Material materials with Dissipation factor, 100Hz of 3E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 4.5E-3 [-] Show Material materials with Dissipation factor, 1MHz of 4.5E-3 [-] | IEC 62631-2-1 |
Surface resistivity | 23.0 °C | 1.00E+15 Ω/sq Show Material materials with Surface resistivity of 1.00E+15 Ω/sq | min. | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt volume-flow rate | 13 cm³/10min Show Material materials with Melt volume-flow rate of 13 cm³/10min | ISO 1133 | |
Shrinkage | 23.0 °C | 1.9 % Show Material materials with Shrinkage of 1.9 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.8 % Show Material materials with Shrinkage, transverse of 1.8 % | ISO 294-4, 2577 |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 215°C, Min. melt temperature: 210°C, Max. melt temperature: 220°C, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 80-100MPa, Hold pressure time: 7.5s/mm | |