General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.37 g/cm³ Show Material materials with Density of 1.37 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 2 GPa Show Material materials with Elastic modulus of 2 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 29 % Show Material materials with Elongation of 29 % | ISO 527-1/-2 | 50mm/min |
Elongation at yield | 23.0 °C | 20 % Show Material materials with Elongation at yield of 20 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 2 GPa Show Material materials with Flexural modulus of 2 GPa | ISO 178 |
Hardness, Rockwell M | 23.0 °C | 69 [-] Show Material materials with Hardness, Rockwell M of 69 [-] | ISO 2039-2 |
Hardness, Rockwell R | 23.0 °C | 116 [-] Show Material materials with Hardness, Rockwell R of 116 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -6.0 °C | 8 kJ/m² Show Material materials with Impact strength, Charpy notched of 8 kJ/m² | ISO 179/1eA |
23.0 °C | 15 kJ/m² Show Material materials with Impact strength, Charpy notched of 15 kJ/m² | ISO 179/1eA | |
Poisson's ratio | 23.0 °C | 0.4 [-] Show Material materials with Poisson's ratio of 0.4 [-] | |
Yield strength | 23.0 °C | 54 MPa Show Material materials with Yield strength of 54 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.1E-4 1/K Show Material materials with Coefficient of thermal expansion of 1.1E-4 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.2E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 136 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 136 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 78 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 78 °C | ISO 75-1/-2 | |||
Vicat softening temperature | 172 °C Show Material materials with Vicat softening temperature of 172 °C | ISO 306 | 90°F, 2 lbf | |||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 6 g/10min Show Material materials with Melt mass-flow rate of 6 g/10min | ISO 1133 | 190°C/2.16kg | |
Shrinkage | 23.0 °C | 1.3 % Show Material materials with Shrinkage of 1.3 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.5 % Show Material materials with Shrinkage, transverse of 1.5 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 4-8h, Processing Moisture Content: ≤0.05%, Melt Temperature Optimum: 205°C, Min. melt temperature: 200°C, Max. melt temperature: 210°C, Mold Temperature Optimum: 50°C, Min. mold temperature: 40°C, Max. mold temperature: 60°C, Hold pressure range: 60-80MPa, Hold pressure time: 7.5s/mm |