General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.41 g/cm³ Show Material materials with Density of 1.41 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 3 GPa Show Material materials with Elastic modulus of 3 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 40 % Show Material materials with Elongation of 40 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 21 % Show Material materials with Elongation at yield of 21 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 2.9 GPa Show Material materials with Flexural modulus of 2.9 GPa | ISO 178 |
Hardness, Rockwell M | 23.0 °C | 84 [-] Show Material materials with Hardness, Rockwell M of 84 [-] | ISO 2039-2 |
Hardness, Rockwell R | 23.0 °C | 117 [-] Show Material materials with Hardness, Rockwell R of 117 [-] | ISO 2039-2 |
Impact strength, Charpy notched | 23.0 °C | 8.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 8.5 kJ/m² | ISO 179/1eA |
Impact strength, Charpy unnotched | 23.0 °C | 270 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 270 kJ/m² | ISO 179/1eU |
Poisson's ratio | 23.0 °C | 0.37 [-] Show Material materials with Poisson's ratio of 0.37 [-] | |
Yield strength | 23.0 °C | 66 MPa Show Material materials with Yield strength of 66 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1E-4 1/K Show Material materials with Coefficient of thermal expansion of 1E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.1E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.1E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Heat deflection temperature, 0.45 MPa | 158 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 158 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 96 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 96 °C | ISO 75-1/-2 | |||
Melting point | 176 °C Show Material materials with Melting point of 176 °C | ISO 11357-1/-3 | 18°F/min | |||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Technological properties
Property | ||
---|---|---|
Fillers | 20% Silicone Fluid |