General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.14 g/cm³ Show Material materials with Density of 1.14 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 2.8 % Show Material materials with Water absorption of 2.8 % | Sim. to ISO 62 | Immersion 24h |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 3.1 GPa Show Material materials with Elastic modulus of 3.1 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 16 % Show Material materials with Elongation of 16 % | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 4.5 % Show Material materials with Elongation at yield of 4.5 % | ISO 527-1/-2 | ||
Flexural modulus | 23.0 °C | 2.8 GPa Show Material materials with Flexural modulus of 2.8 GPa | ISO 178 | ||
Hardness, Ball Indentation | 23.0 °C | 185 MPa Show Material materials with Hardness, Ball Indentation of 185 MPa | ISO 2039-1 | ||
Hardness, Rockwell R | 23.0 °C | 121 [-] Show Material materials with Hardness, Rockwell R of 121 [-] | ISO 2039-2 | ||
Impact strength, Charpy notched | 23.0 °C | 5 kJ/m² Show Material materials with Impact strength, Charpy notched of 5 kJ/m² | ISO 179/1eA | ||
Impact strength, Izod unnotched | -40.0 °C | 5 kJ/m² Show Material materials with Impact strength, Izod unnotched of 5 kJ/m² | ISO 180/1A | ||
23.0 °C | 6 kJ/m² Show Material materials with Impact strength, Izod unnotched of 6 kJ/m² | ISO 180/1A | |||
Poisson's ratio | 23.0 °C | 0.37 [-] Show Material materials with Poisson's ratio of 0.37 [-] | |||
Yield strength | 23.0 °C | 85 MPa Show Material materials with Yield strength of 85 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy unnotched | No Break @ 23°C, ISO 179/1eU |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1E-4 1/K Show Material materials with Coefficient of thermal expansion of 1E-4 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.1E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.1E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 200 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 200 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 70 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 70 °C | ISO 75-1/-2 | |||
Melting point | 263 °C Show Material materials with Melting point of 263 °C | ISO 11357-1/-3 | 18°F/min | |||
Specific heat capacity | 23.0 °C | 2790 J/(kg·K) Show Material materials with Specific heat capacity of 2790 J/(kg·K) | of melt | ||
Thermal diffusivity | 23.0 °C | 0 mm²/s Show Material materials with Thermal diffusivity of 0 mm²/s | |||
Flammability | Burning Behav. at 60mil nom. thickn.: V-2 class, Thickness tested: 1.5 mm, Burning Behav. at thickness h: V-2 class, Thickness tested: 0.4 mm, Glow Wire Flammability Index, 15mil: 850 °C, Glow Wire Flammability Index, 30mil: 850 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 725 °C, Glow Wire Ignition Temperature, 15mil: 725 °C, Glow Wire Ignition Temperature, 40mil: 725 °C, Glow Wire Ignition Temperature, 60mil: 725 °C, Glow Wire Ignition Temperature, 80mil: 725 °C, Glow Wire Ignition Temperature, 120mil: 725 °C, Glow Wire Temperature, No Flame, 30mil: 700 °C, Glow Wire Temperature, No Flame, 40mil: 700 °C, Glow Wire Temperature, No Flame, 60mil: 700 °C, Glow Wire Temperature, No Flame, 80mil: 700 °C, Glow Wire Temperature, No Flame, 120mil: 700 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 1MHz | 23.0 °C | 3.5 [-] Show Material materials with Dielectric constant, 1MHz of 3.5 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 31 kV/mm Show Material materials with Dielectric strength of 31 kV/mm | IEC 60243-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+14 Ω·cm Show Material materials with Volume resistivity of 1.00E+14 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.4m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm, Ejection temperature: 200°C |