General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.47 g/cm³ Show Material materials with Density of 1.47 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 5 % Show Material materials with Water absorption of 5 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 10 GPa Show Material materials with Elastic modulus of 10 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2.2 % Show Material materials with Elongation of 2.2 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 9.5 GPa Show Material materials with Flexural modulus of 9.5 GPa | ISO 178 |
Flexural strength | 23.0 °C | 210 MPa Show Material materials with Flexural strength of 210 MPa | ISO 178 |
Impact strength, Charpy notched | -6.0 °C | 4 kJ/m² Show Material materials with Impact strength, Charpy notched of 4 kJ/m² | ISO 179/1eA |
23.0 °C | 4.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 4.5 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 40 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 40 kJ/m² | ISO 179/1eU |
23.0 °C | 45 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 45 kJ/m² | ISO 179/1eU | |
Impact strength, Izod unnotched | -30.0 °C | 4 kJ/m² Show Material materials with Impact strength, Izod unnotched of 4 kJ/m² | ISO 180/1A |
23.0 °C | 4 kJ/m² Show Material materials with Impact strength, Izod unnotched of 4 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 160 MPa Show Material materials with Tensile strength of 160 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 3.1E-5 1/K Show Material materials with Coefficient of thermal expansion of 3.1E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.3E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.3E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Glass transition temperature | 70 °C Show Material materials with Glass transition temperature of 70 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 256 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 256 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 240 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 240 °C | ISO 75-1/-2 | |||
Melting point | 262 °C Show Material materials with Melting point of 262 °C | ISO 11357-1/-3 | 18°F/min | |||
Specific heat capacity | 23.0 °C | 1900 J/(kg·K) Show Material materials with Specific heat capacity of 1900 J/(kg·K) | of melt | ||
Vicat softening temperature | 250 °C Show Material materials with Vicat softening temperature of 250 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: 28 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 100Hz | 23.0 °C | 4.9 [-] Show Material materials with Dielectric constant, 100Hz of 4.9 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 4.8 [-] Show Material materials with Dielectric constant, 1MHz of 4.8 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 28 kV/mm Show Material materials with Dielectric strength of 28 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 100Hz of 0.01 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 62631-2-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 40% Glass Fiber and Mineral Powder | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.15m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |