General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.06 g/cm³ Show Material materials with Density of 1.06 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.4 % Show Material materials with Water absorption of 0.4 % | Sim. to ISO 62 | Immersion 24h |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.4 GPa Show Material materials with Elastic modulus of 2.4 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 17 % Show Material materials with Elongation of 17 % | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 4.5 % Show Material materials with Elongation at yield of 4.5 % | ISO 527-1/-2 | ||
Flexural modulus | 23.0 °C | 2.1 GPa Show Material materials with Flexural modulus of 2.1 GPa | ISO 178 | ||
Hardness, Rockwell R | 23.0 °C | 114 [-] Show Material materials with Hardness, Rockwell R of 114 [-] | ISO 2039-2 | ||
Impact strength, Charpy notched | -6.0 °C | 3.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 3.5 kJ/m² | ISO 179/1eA | ||
23.0 °C | 3.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 3.5 kJ/m² | ISO 179/1eA | |||
Impact strength, Izod unnotched | -30.0 °C | 4.5 kJ/m² Show Material materials with Impact strength, Izod unnotched of 4.5 kJ/m² | ISO 180/1A | ||
23.0 °C | 4 kJ/m² Show Material materials with Impact strength, Izod unnotched of 4 kJ/m² | ISO 180/1A | |||
Poisson's ratio | 23.0 °C | 0.38 [-] Show Material materials with Poisson's ratio of 0.38 [-] | |||
Yield strength | 23.0 °C | 62 MPa Show Material materials with Yield strength of 62 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy unnotched | No Break @ 23,-6°C, ISO 179/1eA |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.6E-4 1/K Show Material materials with Coefficient of thermal expansion of 1.6E-4 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.8E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.8E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Glass transition temperature | 65 °C Show Material materials with Glass transition temperature of 65 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 135 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 135 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 62 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 62 °C | ISO 75-1/-2 | |||
Melting point | 218 °C Show Material materials with Melting point of 218 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 105 °C Show Material materials with Relative temperature index, electrical of 105 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 65 °C Show Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | 120mil | |||
Specific heat capacity | 23.0 °C | 2750 J/(kg·K) Show Material materials with Specific heat capacity of 2750 J/(kg·K) | of melt | ||
Thermal diffusivity | 23.0 °C | 0 mm²/s Show Material materials with Thermal diffusivity of 0 mm²/s | |||
Vicat softening temperature | 181 °C Show Material materials with Vicat softening temperature of 181 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: V-2 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-2 class, Thickness tested: 0.85 mm, UL recognition: yes -, Oxygen index: 27 %, Glow Wire Flammability Index, 15mil: 960 °C, Glow Wire Flammability Index, 30mil: 960 °C, Glow Wire Flammability Index, 40mil: 960 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 80mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 725 °C, Glow Wire Ignition Temperature, 15mil: 725 °C, Glow Wire Ignition Temperature, 40mil: 725 °C, Glow Wire Ignition Temperature, 60mil: 725 °C, Glow Wire Ignition Temperature, 80mil: 725 °C, Glow Wire Ignition Temperature, 120mil: 725 °C, Glow Wire Temperature, No Flame, 30mil: 700 °C, Glow Wire Temperature, No Flame, 40mil: 700 °C, Glow Wire Temperature, No Flame, 60mil: 700 °C, Glow Wire Temperature, No Flame, 80mil: 700 °C, Glow Wire Temperature, No Flame, 120mil: 700 °C, FMVSS Class: DNI - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Dielectric strength | 23.0 °C | 30 kV/mm Show Material materials with Dielectric strength of 30 kV/mm | IEC 60243-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 35 g/10min Show Material materials with Melt mass-flow rate of 35 g/10min | ISO 1133 | 230°C/1kg | |
Shrinkage | 23.0 °C | 1.3 % Show Material materials with Shrinkage of 1.3 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 1.4 % Show Material materials with Shrinkage, transverse of 1.4 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.15%, Min. melt temperature: 230°C, Max. melt temperature: 290°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C |