General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.56 g/cm³ Show Material materials with Density of 1.56 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.05 % Show Material materials with Water absorption of 0.05 % | Sim. to ISO 62 | Immersion 24h |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Compressive strength | 23.0 °C | 230 MPa Show Material materials with Compressive strength of 230 MPa | ISO 604 |
Elastic modulus | 23.0 °C | 10.2 GPa Show Material materials with Elastic modulus of 10.2 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2.1 % Show Material materials with Elongation of 2.1 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 8.94 GPa Show Material materials with Flexural modulus of 8.94 GPa | ISO 178 |
Flexural strength | 23.0 °C | 210 MPa Show Material materials with Flexural strength of 210 MPa | ISO 178 |
Hardness, Ball Indentation | 23.0 °C | 221 MPa Show Material materials with Hardness, Ball Indentation of 221 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -40.0 °C | 8 kJ/m² Show Material materials with Impact strength, Charpy notched of 8 kJ/m² | ISO 179/1eA |
-6.0 °C | 8.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 8.5 kJ/m² | ISO 179/1eA | |
23.0 °C | 9.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 9.5 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -40.0 °C | 45 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 45 kJ/m² | ISO 179/1eU |
23.0 °C | 52 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 52 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | -40.0 °C | 35 kJ/m² Show Material materials with Impact strength, Izod notched of 35 kJ/m² | ISO 180/1U |
23.0 °C | 45 kJ/m² Show Material materials with Impact strength, Izod notched of 45 kJ/m² | ISO 180/1U | |
Impact strength, Izod unnotched | -40.0 °C | 8.5 kJ/m² Show Material materials with Impact strength, Izod unnotched of 8.5 kJ/m² | ISO 180/1A |
23.0 °C | 9.5 kJ/m² Show Material materials with Impact strength, Izod unnotched of 9.5 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 150 MPa Show Material materials with Tensile strength of 150 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 244 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 244 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 221 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 221 °C | ISO 75-1/-2 | |||
Melting point | 250 °C Show Material materials with Melting point of 250 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical impact | 140 °C Show Material materials with Relative temperature index, mechanical impact of 140 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 240mil | |||
Thermal conductivity | 23.0 °C | 0.29 W/(m·K) Show Material materials with Thermal conductivity of 0.29 W/(m·K) | of solid | ||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.81 mm, UL recognition: yes -, Thickness tested: 0.75 mm, UL recognition: yes -, Glow Wire Flammability Index, 80mil: 800 °C, Glow Wire Flammability Index, 120mil: 900 °C, Glow Wire Ignition Temperature, 80mil: 825 °C, Glow Wire Ignition Temperature, 120mil: 825 °C, Glow Wire Temperature, No Flame, 40mil: 750 °C, Glow Wire Temperature, No Flame, 60mil: 750 °C, Glow Wire Temperature, No Flame, 80mil: 750 °C, Glow Wire Temperature, No Flame, 120mil: 825 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 38 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 250 V Show Material materials with Comparative tracking index of 250 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 4.5 [-] Show Material materials with Dielectric constant, 100Hz of 4.5 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 4.2 [-] Show Material materials with Dielectric constant, 1MHz of 4.2 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 22 kV/mm Show Material materials with Dielectric strength of 22 kV/mm | IEC 60243-1 | Short Time, 23°C, 2mm |
Dissipation factor, 100Hz | 23.0 °C | 0.03 [-] Show Material materials with Dissipation factor, 100Hz of 0.03 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Surface resistivity | 23.0 °C | 1.00E+15 Ω/sq Show Material materials with Surface resistivity of 1.00E+15 Ω/sq | min. | IEC 62631-3-2 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 30% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 285°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 120°C, Min. mold temperature: 110°C, Max. mold temperature: 130°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |