PET FC51 BK507

Want to keep this datasheet? Save it now in your required format

Description

Dupont® PET FC51 BK507 is a 40% Mineral/Glass Reinforced, Flame Retardant, Polyethylene Terephthalate

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.72 g/cm³

Show Material materials with Density of 1.72 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

11 GPa

Show Material materials with Elastic modulus of 11 GPa

ISO 527-1/-2

Elongation

23.0 °C

1.8 %

Show Material materials with Elongation of 1.8 %

ISO 527-1/-2

Flexural modulus

23.0 °C

9.6 GPa

Show Material materials with Flexural modulus of 9.6 GPa

ISO 178

Flexural strength

23.0 °C

170 MPa

Show Material materials with Flexural strength of 170 MPa

ISO 178

Impact strength, Charpy notched

23.0 °C

6 kJ/m²

Show Material materials with Impact strength, Charpy notched of 6 kJ/m²

ISO 179/1eA

Poisson's ratio

23.0 °C

0.34 [-]

Show Material materials with Poisson's ratio of 0.34 [-]

Tensile strength

23.0 °C

110 MPa

Show Material materials with Tensile strength of 110 MPa

ISO 527-1/-2

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

2.5E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.5E-5 1/K

ISO 11359-1/-2

Coefficient of thermal expansion, transverse

23.0 °C

7.8E-5 1/K

Show Material materials with Coefficient of thermal expansion, transverse of 7.8E-5 1/K

ISO 11359-1/-2

Heat deflection temperature, 1.80 MPa

214 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 214 °C

ISO 75-1/-2

Relative temperature index, electrical

150 °C

Show Material materials with Relative temperature index, electrical of 150 °C

UL 746B | 120mil

Relative temperature index, mechanical impact

150 °C

Show Material materials with Relative temperature index, mechanical impact of 150 °C

UL 746B | 120mil

Relative temperature index, mechanical strength

150 °C

Show Material materials with Relative temperature index, mechanical strength of 150 °C

UL 746B | 120mil

Flammability

Burning Behav. at 60mil nom. thickn.: V-1 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-1 class, Thickness tested: 3 mm, UL recognition: yes -

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

3 V

Show Material materials with Comparative tracking index of 3 V

UL 746A

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.2 %

Show Material materials with Shrinkage of 0.2 %

ISO 294-4, 2577

Shrinkage, transverse

23.0 °C

1 %

Show Material materials with Shrinkage, transverse of 1 %

ISO 294-4, 2577

Technological properties

Property
Fillers

40% Glass Fiber and Mineral Powder

Processing methods

Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 280°C, Min. melt temperature: 270°C, Max. melt temperature: 290°C, Mold Temperature Optimum: 120°C, Min. mold temperature: 100°C, Max. mold temperature: 130°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C