General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.68 g/cm³ Show Material materials with Density of 1.68 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.75 % Show Material materials with Water absorption of 0.75 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Compressive strength | 23.0 °C | 200 MPa Show Material materials with Compressive strength of 200 MPa | ISO 604 |
Elastic modulus | 23.0 °C | 11.5 GPa Show Material materials with Elastic modulus of 11.5 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2 % Show Material materials with Elongation of 2 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 10.5 GPa Show Material materials with Flexural modulus of 10.5 GPa | ISO 178 |
Impact strength, Charpy notched | -6.0 °C | 9 kJ/m² Show Material materials with Impact strength, Charpy notched of 9 kJ/m² | ISO 179/1eA |
23.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 40 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 40 kJ/m² | ISO 179/1eU |
23.0 °C | 40 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 40 kJ/m² | ISO 179/1eU | |
Poisson's ratio | 23.0 °C | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | |
Shear strength | 23.0 °C | 60 MPa Show Material materials with Shear strength of 60 MPa | ASTM D 732 |
Tensile strength | 23.0 °C | 135 MPa Show Material materials with Tensile strength of 135 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.2E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.2E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 6.8E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 6.8E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Heat deflection temperature, 0.45 MPa | 243 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 243 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 225 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 225 °C | ISO 75-1/-2 | |||
Melting point | 252 °C Show Material materials with Melting point of 252 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 155 °C Show Material materials with Relative temperature index, electrical of 155 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 155 °C Show Material materials with Relative temperature index, mechanical impact of 155 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 155 °C Show Material materials with Relative temperature index, mechanical strength of 155 °C | UL 746B | 120mil | |||
Specific heat capacity | 23.0 °C | 1720 J/(kg·K) Show Material materials with Specific heat capacity of 1720 J/(kg·K) | of melt | ||
Thermal diffusivity | 23.0 °C | 0 mm²/s Show Material materials with Thermal diffusivity of 0 mm²/s | |||
Vicat softening temperature | 220 °C Show Material materials with Vicat softening temperature of 220 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 0.35 mm, UL recognition: yes -, Burning Behav. 5V at thickness h: 5VA class, Thickness tested: 1.5 mm, UL recognition: yes -, Oxygen index: 33 %, Glow Wire Flammability Index, 30mil: 960 °C, Glow Wire Flammability Index, 40mil: 960 °C, Glow Wire Flammability Index, 80mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 800 °C, Glow Wire Ignition Temperature, 40mil: 800 °C, Glow Wire Ignition Temperature, 60mil: 800 °C, Glow Wire Ignition Temperature, 80mil: 850 °C, Glow Wire Ignition Temperature, 120mil: 925 °C, Glow Wire Temperature, No Flame, 40mil: 800 °C, Glow Wire Temperature, No Flame, 80mil: 775 °C, FMVSS Class: DNI -, Railway classification: R23 -, Railway classification rating: HL1 - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 2 V Show Material materials with Comparative tracking index of 2 V | UL 746A |
Dielectric constant, 100Hz | 23.0 °C | 4.8 [-] Show Material materials with Dielectric constant, 100Hz of 4.8 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 4.3 [-] Show Material materials with Dielectric constant, 1MHz of 4.3 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 39 kV/mm Show Material materials with Dielectric strength of 39 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 7E-3 [-] Show Material materials with Dissipation factor, 100Hz of 7E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 62631-2-1 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Material materials with Surface resistivity of 1.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 30% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 280°C, Min. melt temperature: 270°C, Max. melt temperature: 290°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 110°C, Min. mold temperature: 100°C, Max. mold temperature: 120°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |