General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.45 g/cm³ Show Material materials with Density of 1.45 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 5.7 % Show Material materials with Water absorption of 5.7 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 5.8 GPa Show Material materials with Elastic modulus of 5.8 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 8 % Show Material materials with Elongation of 8 % | ISO 527-1/-2 |
Impact strength, Charpy notched | 23.0 °C | 5.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 5.5 kJ/m² | ISO 179/1eA |
Impact strength, Charpy unnotched | 23.0 °C | 115 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 115 kJ/m² | ISO 179/1eU |
Impact strength, Izod unnotched | 23.0 °C | 5 kJ/m² Show Material materials with Impact strength, Izod unnotched of 5 kJ/m² | ISO 180/1A |
Poisson's ratio | 23.0 °C | 0.35 [-] Show Material materials with Poisson's ratio of 0.35 [-] | |
Tensile strength | 23.0 °C | 87 MPa Show Material materials with Tensile strength of 87 MPa | ISO 527-1/-2 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 95 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 95 °C | ISO 75-1/-2 | |
Melting point | 256 °C Show Material materials with Melting point of 256 °C | ISO 11357-1/-3 | 18°F/min | |
Relative temperature index, electrical | 65 °C Show Material materials with Relative temperature index, electrical of 65 °C | UL 746B | 120mil | |
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 120mil | |
Relative temperature index, mechanical strength | 65 °C Show Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | 120mil | |
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.81 mm, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 40% Mineral Powder | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |