General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.23 g/cm³ Show Material materials with Density of 1.23 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 7.7 % Show Material materials with Water absorption of 7.7 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 3.8 GPa Show Material materials with Elastic modulus of 3.8 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 21 % Show Material materials with Elongation of 21 % | ISO 527-1/-2 |
Impact strength, Charpy notched | -6.0 °C | 6 kJ/m² Show Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO 179/1eA |
23.0 °C | 7.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 7.5 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | 23.0 °C | 100 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 100 kJ/m² | ISO 179/1eU |
Impact strength, Izod unnotched | 23.0 °C | 6 kJ/m² Show Material materials with Impact strength, Izod unnotched of 6 kJ/m² | ISO 180/1A |
Poisson's ratio | 23.0 °C | 0.36 [-] Show Material materials with Poisson's ratio of 0.36 [-] | |
Tensile strength | 23.0 °C | 76 MPa Show Material materials with Tensile strength of 76 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1E-4 1/K Show Material materials with Coefficient of thermal expansion of 1E-4 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1E-4 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 212 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 212 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 75 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 75 °C | ISO 75-1/-2 | |||
Melting point | 263 °C Show Material materials with Melting point of 263 °C | ISO 11357-1/-3 | 18°F/min | |||
Specific heat capacity | 23.0 °C | 2320 J/(kg·K) Show Material materials with Specific heat capacity of 2320 J/(kg·K) | of melt | ||
Vicat softening temperature | 235 °C Show Material materials with Vicat softening temperature of 235 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 575 V Show Material materials with Comparative tracking index of 575 V | IEC 60112 |
Dielectric strength | 23.0 °C | 40 kV/mm Show Material materials with Dielectric strength of 40 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 100Hz of 0.02 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 15% Mineral Powder | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |