Zytel® 70G33HSL BK083

Alternative and trade names
PA66-GF33
Want to keep this datasheet? Save it now in your required format

Description

Zytel® 70G33HSL BK083 is a 33% Glass Reinforced, Heat Stabilized, Polyamide 66

Equivalent Materials

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.39 g/cm³

Show Material materials with Density of 1.39 g/cm³

ISO 1183

Water absorption

23.0 °C

5.7 %

Show Material materials with Water absorption of 5.7 %

Sim. to ISO 62 | 80mil

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

11 GPa

Show Material materials with Elastic modulus of 11 GPa

ISO 527-1/-2

Elongation

23.0 °C

3.5 %

Show Material materials with Elongation of 3.5 %

ISO 527-1/-2

Impact strength, Charpy notched

-6.0 °C

12 kJ/m²

Show Material materials with Impact strength, Charpy notched of 12 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

-6.0 °C

90 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 90 kJ/m²

ISO 179/1eU

23.0 °C

90 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 90 kJ/m²

ISO 179/1eU

Poisson's ratio

23.0 °C

0.34 [-]

Show Material materials with Poisson's ratio of 0.34 [-]

Tensile strength

23.0 °C

200 MPa

Show Material materials with Tensile strength of 200 MPa

ISO 527-1/-2

Thermal

PropertyTemperatureValueComment

Glass transition temperature

80 °C

Show Material materials with Glass transition temperature of 80 °C

ISO 11357-1/-2 | 18°F/min

Heat deflection temperature, 0.45 MPa

260 °C

Show Material materials with Heat deflection temperature, 0.45 MPa of 260 °C

ISO 75-1/-2

Heat deflection temperature, 1.80 MPa

250 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 250 °C

ISO 75-1/-2

Melting point

263 °C

Show Material materials with Melting point of 263 °C

ISO 11357-1/-3 | 18°F/min

Relative temperature index, electrical

130 °C

Show Material materials with Relative temperature index, electrical of 130 °C

UL 746B | 120mil

Relative temperature index, mechanical impact

105 °C

Show Material materials with Relative temperature index, mechanical impact of 105 °C

UL 746B | 120mil

Relative temperature index, mechanical strength

130 °C

Show Material materials with Relative temperature index, mechanical strength of 130 °C

UL 746B | 120mil

Specific heat capacity

23.0 °C

1330 J/(kg·K)

Show Material materials with Specific heat capacity of 1330 J/(kg·K)

of solid

Flammability

Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.7 mm, UL recognition: yes -, Oxygen index: 24 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Electrical

PropertyTemperatureValueComment

Comparative tracking index

23.0 °C

600 V

Show Material materials with Comparative tracking index of 600 V

IEC 60112

Volume resistivity

23.0 °C

1.00E+15 Ω·cm

Show Material materials with Volume resistivity of 1.00E+15 Ω·cm

min. | IEC 62631-3-1

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.3 %

Show Material materials with Shrinkage of 0.3 %

ISO 294-4, 2577

Shrinkage, transverse

23.0 °C

1.1 %

Show Material materials with Shrinkage, transverse of 1.1 %

ISO 294-4, 2577

Technological properties

Property
Fillers

33% Glass Fiber

Processing methods

Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C