Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.39 g/cm³ Show Material materials with Density of 1.39 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 5.7 % Show Material materials with Water absorption of 5.7 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 11 GPa Show Material materials with Elastic modulus of 11 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 3 % Show Material materials with Elongation of 3 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 9.3 GPa Show Material materials with Flexural modulus of 9.3 GPa | ISO 178 |
Impact strength, Charpy notched | -40.0 °C | 9 kJ/m² Show Material materials with Impact strength, Charpy notched of 9 kJ/m² | ISO 179/1eA |
23.0 °C | 13 kJ/m² Show Material materials with Impact strength, Charpy notched of 13 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | 23.0 °C | 80 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 80 kJ/m² | ISO 179/1eU |
Impact strength, Izod unnotched | -40.0 °C | 10 kJ/m² Show Material materials with Impact strength, Izod unnotched of 10 kJ/m² | ISO 180/1A |
23.0 °C | 12 kJ/m² Show Material materials with Impact strength, Izod unnotched of 12 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 200 MPa Show Material materials with Tensile strength of 200 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.8E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.8E-5 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 8.3E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 8.3E-5 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 261 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 261 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 252 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 252 °C | ISO 75-1/-2 | |||
Melting point | 262 °C Show Material materials with Melting point of 262 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 120 °C Show Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | 120mil | |||
Flammability | Burning Behav. at thickness h: HB class, Thickness tested: 0.71 mm, FMVSS Class: B -, Burning rate, Thickness 1 mm: 35 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 33% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |