General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.65 g/cm³ Show Material materials with Density of 1.65 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 11 GPa Show Material materials with Elastic modulus of 11 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2 % Show Material materials with Elongation of 2 % | ISO 527-1/-2 |
Impact strength, Charpy notched | 23.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA |
Impact strength, Charpy unnotched | 23.0 °C | 40 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 40 kJ/m² | ISO 179/1eU |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 155 MPa Show Material materials with Tensile strength of 155 MPa | ISO 527-1/-2 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 230 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 230 °C | ISO 75-1/-2 | |
Melting point | 250 °C Show Material materials with Melting point of 250 °C | ISO 11357-1/-3 | 18°F/min | |
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 120mil | |
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 120mil | |
Flammability | Burning Behav. at thickness h: V-2 class, Thickness tested: 0.8 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 200 V Show Material materials with Comparative tracking index of 200 V | IEC 60112 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt viscosity | 280.0 °C | 205 Pa·s Show Material materials with Melt viscosity of 205 Pa·s | ISO 11443 | @ 1000 sec-1, 280°C |
Shrinkage | 23.0 °C | 0.2 % Show Material materials with Shrinkage of 0.2 % | ISO 294-4, 2577 |
Shrinkage, transverse | 23.0 °C | 0.8 % Show Material materials with Shrinkage, transverse of 0.8 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Fillers | 25% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 280°C, Min. melt temperature: 270°C, Max. melt temperature: 290°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 140°C, Min. mold temperature: 120°C, Max. mold temperature: 140°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |