General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.14 g/cm³ Show Material materials with Density of 1.14 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 1.2 % Show Material materials with Water absorption of 1.2 % | Sim. to ISO 62 | Immersion 24h |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 3.1 GPa Show Material materials with Elastic modulus of 3.1 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 45 % Show Material materials with Elongation of 45 % | ISO 527-1/-2 | 50mm/min | ||
Elongation at yield | 23.0 °C | 4.3 % Show Material materials with Elongation at yield of 4.3 % | ISO 527-1/-2 | ||
Flexural modulus | 23.0 °C | 2.8 GPa Show Material materials with Flexural modulus of 2.8 GPa | ISO 178 | ||
Flexural strength | 23.0 °C | 90 MPa Show Material materials with Flexural strength of 90 MPa | ISO 178 | ||
Hardness, Ball Indentation | 23.0 °C | 160 MPa Show Material materials with Hardness, Ball Indentation of 160 MPa | ISO 2039-1 | ||
Hardness, Rockwell M | 23.0 °C | 79 [-] Show Material materials with Hardness, Rockwell M of 79 [-] | ISO 2039-2 | ||
Hardness, Rockwell R | 23.0 °C | 121 [-] Show Material materials with Hardness, Rockwell R of 121 [-] | ISO 2039-2 | ||
Impact strength, Charpy notched | -6.0 °C | 4.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 4.5 kJ/m² | ISO 179/1eA | ||
23.0 °C | 5.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 5.5 kJ/m² | ISO 179/1eA | |||
Impact strength, Izod unnotched | -40.0 °C | 4 kJ/m² Show Material materials with Impact strength, Izod unnotched of 4 kJ/m² | ISO 180/1A | ||
23.0 °C | 5.5 kJ/m² Show Material materials with Impact strength, Izod unnotched of 5.5 kJ/m² | ISO 180/1A | |||
Poisson's ratio | 23.0 °C | 0.37 [-] Show Material materials with Poisson's ratio of 0.37 [-] | |||
Yield strength | 23.0 °C | 82 MPa Show Material materials with Yield strength of 82 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy unnotched | No Break @ 23°C, ISO 179/1eU | ||||
Impact strength, Izod notched | No Break @ 23°C, ISO 179/1eU |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Glass transition temperature | 65 °C Show Material materials with Glass transition temperature of 65 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 190 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 190 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 70 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 70 °C | ISO 75-1/-2 | |||
Melting point | 262 °C Show Material materials with Melting point of 262 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical impact | 75 °C Show Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical strength | 85 °C Show Material materials with Relative temperature index, mechanical strength of 85 °C | UL 746B | 240mil | |||
Specific heat capacity | 23.0 °C | 1680 J/(kg·K) Show Material materials with Specific heat capacity of 1680 J/(kg·K) | of solid | ||
Thermal conductivity | 23.0 °C | 0.24 W/(m·K) Show Material materials with Thermal conductivity of 0.24 W/(m·K) | of solid | ||
Flammability | Burning Behav. at 60mil nom. thickn.: V-2 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-2 class, Thickness tested: 0.71 mm, UL recognition: yes -, Glow Wire Flammability Index, 30mil: 960 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 725 °C, Glow Wire Ignition Temperature, 60mil: 750 °C, Glow Wire Ignition Temperature, 120mil: 800 °C, Glow Wire Temperature, No Flame, 40mil: 805 °C, Glow Wire Temperature, No Flame, 60mil: 775 °C, Glow Wire Temperature, No Flame, 80mil: 700 °C, FMVSS Class: DNI - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 475 V Show Material materials with Comparative tracking index of 475 V | IEC 60112 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.4m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm, Ejection temperature: 190°C |