General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.57 g/cm³ Show Material materials with Density of 1.57 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.8 % Show Material materials with Water absorption of 0.8 % | Sim. to ISO 62 | Immersion 24h |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Compressive strength | 23.0 °C | 215 MPa Show Material materials with Compressive strength of 215 MPa | ISO 604 |
Elastic modulus | 23.0 °C | 17 GPa Show Material materials with Elastic modulus of 17 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2.4 % Show Material materials with Elongation of 2.4 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 16 GPa Show Material materials with Flexural modulus of 16 GPa | ISO 178 |
Flexural strength | 23.0 °C | 400 MPa Show Material materials with Flexural strength of 400 MPa | ISO 178 |
Hardness, Ball Indentation | 23.0 °C | 300 MPa Show Material materials with Hardness, Ball Indentation of 300 MPa | ISO 2039-1 |
Impact strength, Charpy notched | -6.0 °C | 15 kJ/m² Show Material materials with Impact strength, Charpy notched of 15 kJ/m² | ISO 179/1eA |
23.0 °C | 15 kJ/m² Show Material materials with Impact strength, Charpy notched of 15 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 90 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 90 kJ/m² | ISO 179/1eU |
23.0 °C | 90 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 90 kJ/m² | ISO 179/1eU | |
Poisson's ratio | 23.0 °C | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | |
Shear strength | 23.0 °C | 90 MPa Show Material materials with Shear strength of 90 MPa | ASTM D 732 |
Tensile strength | 23.0 °C | 240 MPa Show Material materials with Tensile strength of 240 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.9E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.9E-5 1/K | ASTM E 831 | 55 - 160°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 6.1E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 6.1E-5 1/K | ASTM E 831 | 23 - 55°C | ||
Glass transition temperature | 65 °C Show Material materials with Glass transition temperature of 65 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 261 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 261 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 255 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 255 °C | ISO 75-1/-2 | |||
Melting point | 262 °C Show Material materials with Melting point of 262 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 120 °C Show Material materials with Relative temperature index, electrical of 120 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | 120mil | |||
Specific heat capacity | 23.0 °C | 1870 J/(kg·K) Show Material materials with Specific heat capacity of 1870 J/(kg·K) | of melt | ||
Thermal conductivity | 23.0 °C | 0.46 W/(m·K) Show Material materials with Thermal conductivity of 0.46 W/(m·K) | of solid | ||
Vicat softening temperature | 255 °C Show Material materials with Vicat softening temperature of 255 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.83 mm, UL recognition: yes -, Oxygen index: 24 %, FMVSS Class: SE - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 500 V Show Material materials with Comparative tracking index of 500 V | IEC 60112 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 50% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |