General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.51 g/cm³ Show Material materials with Density of 1.51 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 10 GPa Show Material materials with Elastic modulus of 10 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2.5 % Show Material materials with Elongation of 2.5 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 9.5 GPa Show Material materials with Flexural modulus of 9.5 GPa | ISO 178 |
Impact strength, Charpy notched | -40.0 °C | 2 kJ/m² Show Material materials with Impact strength, Charpy notched of 2 kJ/m² | ISO 179/1eA |
23.0 °C | 3 kJ/m² Show Material materials with Impact strength, Charpy notched of 3 kJ/m² | ISO 179/1eA | |
Impact strength, Izod unnotched | -40.0 °C | 2.5 kJ/m² Show Material materials with Impact strength, Izod unnotched of 2.5 kJ/m² | ISO 180/1A |
23.0 °C | 3.5 kJ/m² Show Material materials with Impact strength, Izod unnotched of 3.5 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 95 MPa Show Material materials with Tensile strength of 95 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 3.6E-5 1/K Show Material materials with Coefficient of thermal expansion of 3.6E-5 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 6.6E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 6.6E-5 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 240 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 240 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 205 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 205 °C | ISO 75-1/-2 | |||
Melting point | 263 °C Show Material materials with Melting point of 263 °C | ISO 11357-1/-3 | 18°F/min | |||
Flammability | Burning Behav. at thickness h: HB class, Thickness tested: 0.71 mm, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 40% Mineral Powder | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |