General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.58 g/cm³ Show Material materials with Density of 1.58 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 10.2 GPa Show Material materials with Elastic modulus of 10.2 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2 % Show Material materials with Elongation of 2 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 9.3 GPa Show Material materials with Flexural modulus of 9.3 GPa | ISO 178 |
Flexural strength | 23.0 °C | 132 MPa Show Material materials with Flexural strength of 132 MPa | ISO 178 |
Impact strength, Charpy notched | -40.0 °C | 4 kJ/m² Show Material materials with Impact strength, Charpy notched of 4 kJ/m² | ISO 179/1eA |
-6.0 °C | 4 kJ/m² Show Material materials with Impact strength, Charpy notched of 4 kJ/m² | ISO 179/1eA | |
23.0 °C | 5.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 5.5 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -40.0 °C | 21.5 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 21.5 kJ/m² | ISO 179/1eU |
23.0 °C | 25 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 25 kJ/m² | ISO 179/1eU | |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 82 MPa Show Material materials with Tensile strength of 82 MPa | ISO 527-1/-2 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 240 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 240 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 200 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 200 °C | ISO 75-1/-2 | |
Melting point | 252 °C Show Material materials with Melting point of 252 °C | ISO 11357-1/-3 | 18°F/min | |
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 120mil | |
Relative temperature index, mechanical impact | 140 °C Show Material materials with Relative temperature index, mechanical impact of 140 °C | UL 746B | 120mil | |
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 120mil | |
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Glow Wire Flammability Index, 30mil: 775 °C, Glow Wire Flammability Index, 60mil: 775 °C, Glow Wire Flammability Index, 120mil: 825 °C, Glow Wire Ignition Temperature, 30mil: 800 °C, Glow Wire Ignition Temperature, 60mil: 800 °C, Glow Wire Ignition Temperature, 120mil: 850 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 1MHz | 23.0 °C | 4 [-] Show Material materials with Dielectric constant, 1MHz of 4 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 25 kV/mm Show Material materials with Dielectric strength of 25 kV/mm | IEC 60243-1 | Short Time, 23°C, 2mm |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 35% Glass Fiber and Mineral Powder | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 285°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 110°C, Min. mold temperature: 100°C, Max. mold temperature: 120°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |