General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.57 g/cm³ Show Material materials with Density of 1.57 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 17 GPa Show Material materials with Elastic modulus of 17 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2.8 % Show Material materials with Elongation of 2.8 % | ISO 527-1/-2 |
Impact strength, Charpy notched | 23.0 °C | 16 kJ/m² Show Material materials with Impact strength, Charpy notched of 16 kJ/m² | ISO 179/1eA |
Impact strength, Charpy unnotched | -6.0 °C | 95 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 95 kJ/m² | ISO 179/1eU |
23.0 °C | 95 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 95 kJ/m² | ISO 179/1eU | |
Poisson's ratio | 23.0 °C | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | |
Tensile strength | 23.0 °C | 240 MPa Show Material materials with Tensile strength of 240 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2E-5 1/K Show Material materials with Coefficient of thermal expansion of 2E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.1E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.1E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Glass transition temperature | 70 °C Show Material materials with Glass transition temperature of 70 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 1.80 MPa | 255 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 255 °C | ISO 75-1/-2 | |||
Melting point | 261 °C Show Material materials with Melting point of 261 °C | ISO 11357-1/-3 | 18°F/min | |||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 50% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |