General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.36 g/cm³ Show Material materials with Density of 1.36 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 6.3 % Show Material materials with Water absorption of 6.3 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 9.5 GPa Show Material materials with Elastic modulus of 9.5 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 3.5 % Show Material materials with Elongation of 3.5 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 8.5 GPa Show Material materials with Flexural modulus of 8.5 GPa | ISO 178 |
Flexural strength | 23.0 °C | 280 MPa Show Material materials with Flexural strength of 280 MPa | ISO 178 |
Hardness, Ball Indentation | 23.0 °C | 230 MPa Show Material materials with Hardness, Ball Indentation of 230 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 121 [-] Show Material materials with Hardness, Rockwell R of 121 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -40.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA |
-6.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA | |
23.0 °C | 16 kJ/m² Show Material materials with Impact strength, Charpy notched of 16 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 80 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 80 kJ/m² | ISO 179/1eU |
23.0 °C | 100 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 100 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | 23.0 °C | 80 kJ/m² Show Material materials with Impact strength, Izod notched of 80 kJ/m² | ISO 180/1U |
Impact strength, Izod unnotched | -30.0 °C | 10 kJ/m² Show Material materials with Impact strength, Izod unnotched of 10 kJ/m² | ISO 180/1A |
23.0 °C | 15 kJ/m² Show Material materials with Impact strength, Izod unnotched of 15 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 190 MPa Show Material materials with Tensile strength of 190 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.6E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.6E-5 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 7.5E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 7.5E-5 1/K | ISO 11359-1/-2 | ||
Glass transition temperature | 60 °C Show Material materials with Glass transition temperature of 60 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 220 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 220 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 210 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 210 °C | ISO 75-1/-2 | |||
Melting point | 221 °C Show Material materials with Melting point of 221 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 65 °C Show Material materials with Relative temperature index, electrical of 65 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 65 °C Show Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | 120mil | |||
Specific heat capacity | 23.0 °C | 2280 J/(kg·K) Show Material materials with Specific heat capacity of 2280 J/(kg·K) | of melt | ||
Thermal diffusivity | 23.0 °C | 0 mm²/s Show Material materials with Thermal diffusivity of 0 mm²/s | |||
Vicat softening temperature | 215 °C Show Material materials with Vicat softening temperature of 215 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Oxygen index: 21 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: 50 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 30% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 270°C, Min. melt temperature: 260°C, Max. melt temperature: 280°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm |