General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.6 g/cm³ Show Material materials with Density of 1.6 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 12.9 GPa Show Material materials with Elastic modulus of 12.9 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 0.9 % Show Material materials with Elongation of 0.9 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 13.1 GPa Show Material materials with Flexural modulus of 13.1 GPa | ISO 178 |
Flexural strength | 23.0 °C | 137 MPa Show Material materials with Flexural strength of 137 MPa | ISO 178 |
Impact strength, Charpy notched | -40.0 °C | 9 kJ/m² Show Material materials with Impact strength, Charpy notched of 9 kJ/m² | ISO 179/1eA |
23.0 °C | 9 kJ/m² Show Material materials with Impact strength, Charpy notched of 9 kJ/m² | ISO 179/1eA | |
Poisson's ratio | 23.0 °C | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | |
Tensile strength | 23.0 °C | 82 MPa Show Material materials with Tensile strength of 82 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.2E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.2E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 9.3E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 9.3E-5 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Heat deflection temperature, 1.80 MPa | 240 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 240 °C | ISO 75-1/-2 | |||
Melting point | 249 °C Show Material materials with Melting point of 249 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 155 °C Show Material materials with Relative temperature index, electrical of 155 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 170 °C Show Material materials with Relative temperature index, mechanical impact of 170 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 170 °C Show Material materials with Relative temperature index, mechanical strength of 170 °C | UL 746B | 120mil | |||
Flammability | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 0.4 mm, UL recognition: yes -, Burning Behav. 5V at thickness h: 5VA class, Thickness tested: 0.75 mm, UL recognition: yes - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric strength | 23.0 °C | 31 kV/mm Show Material materials with Dielectric strength of 31 kV/mm | IEC 60243-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 33% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 280°C, Min. melt temperature: 270°C, Max. melt temperature: 280°C, Min. mold temperature: 120°C, Max. mold temperature: 140°C |