Rynite® RE5264 NC010

Alternative and trade names
PET-GF36

Want to keep this datasheet? Save it now in your required format

Description

Common features of Rynite® thermoplastic polyester include mechanical and physical properties such as excellent balance of strength and stiffness, dimensional stability, creep resistance, heat resistance,high surface gloss and good inherent electrical properties at elevated temperature. It can be processed over a broad temperature range and has excellent flow properties. Rynite® thermoplastic polyester resins aretypically used in demanding applications in the automotive, electrical and electronics, appliances where they successfully replace metals and thermosets, as well as other thermoplastic polymers.Rynite® RE5264 NC010 is a 36% glass reinforced, modified polyethylene terephthalate resin developed for applications that need high burst strength.

This material data has been provided by Matmatch.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.66 g/cm³ Show Material materials with Density of 1.66 g/cm³	ISO 1183

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	14 GPa Show Material materials with Elastic modulus of 14 GPa	ISO 527-1/-2
Elongation	23.0 °C	2 % Show Material materials with Elongation of 2 %	ISO 527-1/-2
Flexural modulus	23.0 °C	12 GPa Show Material materials with Flexural modulus of 12 GPa	ISO 178
Flexural strength	23.0 °C	280 MPa Show Material materials with Flexural strength of 280 MPa	ISO 178
Hardness, Ball Indentation	23.0 °C	225 MPa Show Material materials with Hardness, Ball Indentation of 225 MPa	ISO 2039-1
Hardness, Rockwell R	23.0 °C	120 [-] Show Material materials with Hardness, Rockwell R of 120 [-]	ISO 2039-2
Impact strength, Charpy notched	-40.0 °C	9 kJ/m² Show Material materials with Impact strength, Charpy notched of 9 kJ/m²	ISO 179/1eA
	-6.0 °C	9 kJ/m² Show Material materials with Impact strength, Charpy notched of 9 kJ/m²	ISO 179/1eA
	23.0 °C	9.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 9.5 kJ/m²	ISO 179/1eA

Impact strength, Charpy unnotched	23.0 °C	55 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 55 kJ/m²	ISO 179/1eU
Poisson's ratio	23.0 °C	0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-]
Tensile strength	23.0 °C	190 MPa Show Material materials with Tensile strength of 190 MPa	ISO 527-1/-2

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	2E-5 1/K Show Material materials with Coefficient of thermal expansion of 2E-5 1/K	ISO 11359-1/-2
Coefficient of thermal expansion, transverse	23.0 °C	7E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 7E-5 1/K	ISO 11359-1/-2
Heat deflection temperature, 0.45 MPa		245 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 245 °C	ISO 75-1/-2
Heat deflection temperature, 1.80 MPa		230 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 230 °C	ISO 75-1/-2
Melting point		247 °C Show Material materials with Melting point of 247 °C	ISO 11357-1/-3 \| 18°F/min
Flammability	Glow Wire Flammability Index, 40mil: 750 °C, Glow Wire Flammability Index, 60mil: 750 °C, Glow Wire Flammability Index, 80mil: 750 °C, Glow Wire Flammability Index, 120mil: 850 °C, Glow Wire Ignition Temperature, 40mil: 750 °C, Glow Wire Ignition Temperature, 60mil: 750 °C, Glow Wire Ignition Temperature, 80mil: 750 °C, Glow Wire Ignition Temperature, 120mil: 850 °C, Glow Wire Temperature, No Flame, 40mil: 750 °C, Glow Wire Temperature, No Flame, 60mil: 750 °C, Glow Wire Temperature, No Flame, 80mil: 750 °C, Glow Wire Temperature, No Flame, 120mil: 850 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Electrical

Property	Temperature	Value	Comment
Dielectric strength	23.0 °C	21.5 kV/mm Show Material materials with Dielectric strength of 21.5 kV/mm	IEC 60243-1

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		9 g/10min Show Material materials with Melt mass-flow rate of 9 g/10min	ISO 1133 \| 280°C/2.16kg
Shrinkage	23.0 °C	0.2 % Show Material materials with Shrinkage of 0.2 %	ISO 294-4, 2577
Shrinkage, transverse	23.0 °C	0.9 % Show Material materials with Shrinkage, transverse of 0.9 %	ISO 294-4, 2577

Technological properties

Property
Fillers	36% Glass Fiber
Processing methods	Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.01%, Melt Temperature Optimum: 285°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 140°C, Min. mold temperature: 120°C, Max. mold temperature: 140°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C

Rynite® RE5264 NC010

Description

Ashby charts

Suggested reading

Properties