General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.14 g/cm³ Show Material materials with Density of 1.14 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 3.1 GPa Show Material materials with Elastic modulus of 3.1 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 18 % Show Material materials with Elongation of 18 % | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 4.5 % Show Material materials with Elongation at yield of 4.5 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 2.8 GPa Show Material materials with Flexural modulus of 2.8 GPa | ISO 178 |
Impact strength, Charpy notched | 23.0 °C | 5.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 5.5 kJ/m² | ISO 179/1eA |
Impact strength, Izod unnotched | -40.0 °C | 5 kJ/m² Show Material materials with Impact strength, Izod unnotched of 5 kJ/m² | ISO 180/1A |
23.0 °C | 5.5 kJ/m² Show Material materials with Impact strength, Izod unnotched of 5.5 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.37 [-] Show Material materials with Poisson's ratio of 0.37 [-] | |
Yield strength | 23.0 °C | 82 MPa Show Material materials with Yield strength of 82 MPa | ISO 527-1/-2 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Glass transition temperature | 65 °C Show Material materials with Glass transition temperature of 65 °C | ISO 11357-1/-2 | 18°F/min | |
Heat deflection temperature, 0.45 MPa | 190 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 190 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 70 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 70 °C | ISO 75-1/-2 | |
Melting point | 262 °C Show Material materials with Melting point of 262 °C | ISO 11357-1/-3 | 18°F/min | |
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 240mil | |
Relative temperature index, mechanical impact | 75 °C Show Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | 240mil | |
Relative temperature index, mechanical strength | 85 °C Show Material materials with Relative temperature index, mechanical strength of 85 °C | UL 746B | 240mil | |
Flammability | Burning Behav. at 60mil nom. thickn.: V-2 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-2 class, Thickness tested: 0.71 mm, UL recognition: yes -, Glow Wire Flammability Index, 30mil: 960 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 725 °C, Glow Wire Ignition Temperature, 60mil: 750 °C, Glow Wire Ignition Temperature, 120mil: 800 °C, FMVSS Class: SE - |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.4m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm, Ejection temperature: 190°C |