Rynite® 935SUV BK593

Alternative and trade names
PET-(MD+GF)35
Want to keep this datasheet? Save it now in your required format

Description

Common features of Rynite® thermoplastic polyester include mechanical and physical properties such as excellent balance of strength and stiffness, dimensional stability, creep resistance, heat resistance,high surface gloss and good inherent electrical properties at elevated temperature. It can be processed over a broad temperature range and has excellent flow properties. Rynite® thermoplastic polyester resins aretypically used in demanding applications in the automotive, electrical and electronics, appliances where they successfully replace metals and thermosets, as well as other thermoplastic polymers. Rynite® 935SUV BK593 is a 35% mica/glassreinforced, UV stabilized, modified polyethylene terephthalate resin with low warpage, developed for long-term outdoor applications.

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.57 g/cm³

Show Material materials with Density of 1.57 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

9.7 GPa

Show Material materials with Elastic modulus of 9.7 GPa

ISO 527-1/-2

Elongation

23.0 °C

2.3 %

Show Material materials with Elongation of 2.3 %

ISO 527-1/-2

Impact strength, Charpy notched

23.0 °C

5 kJ/m²

Show Material materials with Impact strength, Charpy notched of 5 kJ/m²

ISO 179/1eA

Impact strength, Charpy unnotched

23.0 °C

24 kJ/m²

Show Material materials with Impact strength, Charpy unnotched of 24 kJ/m²

ISO 179/1eU

Poisson's ratio

23.0 °C

0.34 [-]

Show Material materials with Poisson's ratio of 0.34 [-]

Tensile strength

23.0 °C

80 MPa

Show Material materials with Tensile strength of 80 MPa

ISO 527-1/-2

Thermal

PropertyValueComment

Melting point

252 °C

Show Material materials with Melting point of 252 °C

ISO 11357-1/-3 | 18°F/min

Flammability

Glow Wire Flammability Index, 15mil: 750 °C, Glow Wire Flammability Index, 30mil: 750 °C, Glow Wire Flammability Index, 40mil: 750 °C, Glow Wire Flammability Index, 60mil: 750 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 750 °C, Glow Wire Ignition Temperature, 15mil: 750 °C, Glow Wire Ignition Temperature, 40mil: 750 °C, Glow Wire Ignition Temperature, 60mil: 750 °C, Glow Wire Ignition Temperature, 120mil: 875 °C, Glow Wire Temperature, No Flame, 30mil: 750 °C, Glow Wire Temperature, No Flame, 40mil: 750 °C, Glow Wire Temperature, No Flame, 60mil: 750 °C, Glow Wire Temperature, No Flame, 120mil: 850 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.3 %

Show Material materials with Shrinkage of 0.3 %

ISO 294-4, 2577

Shrinkage, transverse

23.0 °C

0.7 %

Show Material materials with Shrinkage, transverse of 0.7 %

ISO 294-4, 2577

Technological properties

Property
Fillers

35% Glass Fiber and Mineral Powder

Processing methods

Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 285°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 110°C, Min. mold temperature: 100°C, Max. mold temperature: 120°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C