General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.55 g/cm³ Show Material materials with Density of 1.55 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 6.14 GPa Show Material materials with Elastic modulus of 6.14 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2.2 % Show Material materials with Elongation of 2.2 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 6 GPa Show Material materials with Flexural modulus of 6 GPa | ISO 178 |
Flexural strength | 23.0 °C | 160 MPa Show Material materials with Flexural strength of 160 MPa | ISO 178 |
Impact strength, Charpy notched | -40.0 °C | 6 kJ/m² Show Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO 179/1eA |
23.0 °C | 6.2 kJ/m² Show Material materials with Impact strength, Charpy notched of 6.2 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -40.0 °C | 20 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 20 kJ/m² | ISO 179/1eU |
23.0 °C | 32 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 32 kJ/m² | ISO 179/1eU | |
Poisson's ratio | 23.0 °C | 0.35 [-] Show Material materials with Poisson's ratio of 0.35 [-] | |
Tensile strength | 23.0 °C | 100 MPa Show Material materials with Tensile strength of 100 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.9E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.9E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.3E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.3E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Heat deflection temperature, 0.45 MPa | 238 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 238 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 200 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 200 °C | ISO 75-1/-2 | |||
Melting point | 254 °C Show Material materials with Melting point of 254 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 140 °C Show Material materials with Relative temperature index, mechanical impact of 140 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 120mil | |||
Flammability | Burning Behav. at thickness h: V-0 class, Thickness tested: 0.86 mm, UL recognition: yes -, Burning Behav. 5V at thickness h: 5VA class, Thickness tested: 1.5 mm, UL recognition: yes -, Oxygen index: 32 %, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 120mil: 900 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 3 V Show Material materials with Comparative tracking index of 3 V | UL 746A |
Dielectric constant, 100Hz | 23.0 °C | 3.6 [-] Show Material materials with Dielectric constant, 100Hz of 3.6 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 3.5 [-] Show Material materials with Dielectric constant, 1MHz of 3.5 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 40 kV/mm Show Material materials with Dielectric strength of 40 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 100Hz of 0.02 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 62631-2-1 |
Surface resistivity | 23.0 °C | 1.00E+13 Ω/sq Show Material materials with Surface resistivity of 1.00E+13 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 15% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 280°C, Min. melt temperature: 270°C, Max. melt temperature: 290°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 110°C, Min. mold temperature: 100°C, Max. mold temperature: 120°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |