General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.23 g/cm³ Show Material materials with Density of 1.23 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 1.7 % Show Material materials with Water absorption of 1.7 % | Sim. to ISO 62 | Immersion 24h |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 5.5 GPa Show Material materials with Elastic modulus of 5.5 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 3 % Show Material materials with Elongation of 3 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 4.8 GPa Show Material materials with Flexural modulus of 4.8 GPa | ISO 178 |
Impact strength, Charpy notched | -40.0 °C | 4.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 4.5 kJ/m² | ISO 179/1eA |
-6.0 °C | 4.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 4.5 kJ/m² | ISO 179/1eA | |
23.0 °C | 5 kJ/m² Show Material materials with Impact strength, Charpy notched of 5 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 40 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 40 kJ/m² | ISO 179/1eU |
23.0 °C | 40 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 40 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | -30.0 °C | 35 kJ/m² Show Material materials with Impact strength, Izod notched of 35 kJ/m² | ISO 180/1U |
23.0 °C | 40 kJ/m² Show Material materials with Impact strength, Izod notched of 40 kJ/m² | ISO 180/1U | |
Impact strength, Izod unnotched | -40.0 °C | 4.5 kJ/m² Show Material materials with Impact strength, Izod unnotched of 4.5 kJ/m² | ISO 180/1A |
-30.0 °C | 4.5 kJ/m² Show Material materials with Impact strength, Izod unnotched of 4.5 kJ/m² | ISO 180/1A | |
23.0 °C | 4.5 kJ/m² Show Material materials with Impact strength, Izod unnotched of 4.5 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.35 [-] Show Material materials with Poisson's ratio of 0.35 [-] | |
Tensile strength | 23.0 °C | 120 MPa Show Material materials with Tensile strength of 120 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 2.6E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.6E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.5E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.5E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Glass transition temperature | 80 °C Show Material materials with Glass transition temperature of 80 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 255 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 255 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 235 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 235 °C | ISO 75-1/-2 | |||
Melting point | 262 °C Show Material materials with Melting point of 262 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 125 °C Show Material materials with Relative temperature index, electrical of 125 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 120 °C Show Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 125 °C Show Material materials with Relative temperature index, mechanical strength of 125 °C | UL 746B | 120mil | |||
Vicat softening temperature | 205 °C Show Material materials with Vicat softening temperature of 205 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.71 mm, UL recognition: yes -, Oxygen index: 24 %, Glow Wire Flammability Index, 30mil: 650 °C, Glow Wire Flammability Index, 60mil: 650 °C, Glow Wire Flammability Index, 120mil: 800 °C, Glow Wire Ignition Temperature, 30mil: 675 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 27 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 100Hz | 23.0 °C | 3.9 [-] Show Material materials with Dielectric constant, 100Hz of 3.9 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 3.2 [-] Show Material materials with Dielectric constant, 1MHz of 3.2 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 25 kV/mm Show Material materials with Dielectric strength of 25 kV/mm | IEC 60243-1 | Short Time, 2mm |
Dissipation factor, 100Hz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 100Hz of 0.01 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 13% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |