General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.35 g/cm³ Show Material materials with Density of 1.35 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 6.3 % Show Material materials with Water absorption of 6.3 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 4.8 GPa Show Material materials with Elastic modulus of 4.8 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 15 % Show Material materials with Elongation of 15 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 4.8 GPa Show Material materials with Flexural modulus of 4.8 GPa | ISO 178 |
Impact strength, Charpy notched | -6.0 °C | 3.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 3.5 kJ/m² | ISO 179/1eA |
23.0 °C | 5.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 5.5 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 85 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 85 kJ/m² | ISO 179/1eU |
23.0 °C | 110 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 110 kJ/m² | ISO 179/1eU | |
Impact strength, Izod unnotched | -30.0 °C | 4 kJ/m² Show Material materials with Impact strength, Izod unnotched of 4 kJ/m² | ISO 180/1A |
23.0 °C | 5.5 kJ/m² Show Material materials with Impact strength, Izod unnotched of 5.5 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.36 [-] Show Material materials with Poisson's ratio of 0.36 [-] | |
Tensile strength | 23.0 °C | 82 MPa Show Material materials with Tensile strength of 82 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 8.9E-5 1/K Show Material materials with Coefficient of thermal expansion of 8.9E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.1E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.1E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Heat deflection temperature, 0.45 MPa | 195 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 195 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 80 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 80 °C | ISO 75-1/-2 | |||
Melting point | 221 °C Show Material materials with Melting point of 221 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 65 °C Show Material materials with Relative temperature index, electrical of 65 °C | UL 746B | 30mil | |||
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 30mil | |||
Relative temperature index, mechanical strength | 65 °C Show Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | 30mil | |||
Vicat softening temperature | 210 °C Show Material materials with Vicat softening temperature of 210 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | Burning Behav. at thickness h: HB class, Thickness tested: 0.85 mm, UL recognition: yes -, FMVSS Class: SE - |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 30% Mineral Powder | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 270°C, Min. melt temperature: 260°C, Max. melt temperature: 280°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm |