General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.69 g/cm³ Show Material materials with Density of 1.69 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.62 % Show Material materials with Water absorption of 0.62 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Compressive strength | 23.0 °C | 230 MPa Show Material materials with Compressive strength of 230 MPa | ISO 604 |
Elastic modulus | 23.0 °C | 15.5 GPa Show Material materials with Elastic modulus of 15.5 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2 % Show Material materials with Elongation of 2 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 13.5 GPa Show Material materials with Flexural modulus of 13.5 GPa | ISO 178 |
Hardness, Rockwell M | 23.0 °C | 100 [-] Show Material materials with Hardness, Rockwell M of 100 [-] | ISO 2039-2 |
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -6.0 °C | 11 kJ/m² Show Material materials with Impact strength, Charpy notched of 11 kJ/m² | ISO 179/1eA |
23.0 °C | 11 kJ/m² Show Material materials with Impact strength, Charpy notched of 11 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 40 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 40 kJ/m² | ISO 179/1eU |
23.0 °C | 60 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 60 kJ/m² | ISO 179/1eU | |
Impact strength, Izod unnotched | 23.0 °C | 11 kJ/m² Show Material materials with Impact strength, Izod unnotched of 11 kJ/m² | ISO 180/1A |
Poisson's ratio | 23.0 °C | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | |
Shear strength | 23.0 °C | 50 MPa Show Material materials with Shear strength of 50 MPa | ASTM D 732 |
Tensile strength | 23.0 °C | 182 MPa Show Material materials with Tensile strength of 182 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.5E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.5E-5 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 8.3E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 8.3E-5 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 1.80 MPa | 226 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 226 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 8.0 MPa | 180 °C Show Material materials with Heat deflection temperature, 8.0 MPa of 180 °C | ISO 75-1/-2 | |||
Melting point | 252 °C Show Material materials with Melting point of 252 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 140 °C Show Material materials with Relative temperature index, mechanical impact of 140 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 120mil | |||
Thermal conductivity | 23.0 °C | 0.32 W/(m·K) Show Material materials with Thermal conductivity of 0.32 W/(m·K) | of solid | ||
Thermal diffusivity | 23.0 °C | 0 mm²/s Show Material materials with Thermal diffusivity of 0 mm²/s | |||
Vicat softening temperature | 230 °C Show Material materials with Vicat softening temperature of 230 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Oxygen index: 20 %, Glow Wire Flammability Index, 80mil: 750 °C, Glow Wire Flammability Index, 120mil: 850 °C, Glow Wire Ignition Temperature, 120mil: 825 °C, Glow Wire Temperature, No Flame, 40mil: 775 °C, Glow Wire Temperature, No Flame, 60mil: 775 °C, Glow Wire Temperature, No Flame, 80mil: 775 °C, Glow Wire Temperature, No Flame, 120mil: 850 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 2 V Show Material materials with Comparative tracking index of 2 V | UL 746A |
Dielectric constant, 100Hz | 23.0 °C | 4.5 [-] Show Material materials with Dielectric constant, 100Hz of 4.5 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 4.4 [-] Show Material materials with Dielectric constant, 1MHz of 4.4 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 32 kV/mm Show Material materials with Dielectric strength of 32 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 7E-3 [-] Show Material materials with Dissipation factor, 100Hz of 7E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 62631-2-1 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Material materials with Surface resistivity of 1.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 45% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 285°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 120°C, Min. mold temperature: 110°C, Max. mold temperature: 130°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |