General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.41 g/cm³ Show Material materials with Density of 1.41 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 1.1 % Show Material materials with Water absorption of 1.1 % | Sim. to ISO 62 | Immersion 24h |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 11 GPa Show Material materials with Elastic modulus of 11 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 3 % Show Material materials with Elongation of 3 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 9.5 GPa Show Material materials with Flexural modulus of 9.5 GPa | ISO 178 |
Flexural strength | 23.0 °C | 300 MPa Show Material materials with Flexural strength of 300 MPa | ISO 178 |
Hardness, Ball Indentation | 23.0 °C | 285 MPa Show Material materials with Hardness, Ball Indentation of 285 MPa | ISO 2039-1 |
Hardness, Rockwell M | 23.0 °C | 110 [-] Show Material materials with Hardness, Rockwell M of 110 [-] | ISO 2039-2 |
Hardness, Rockwell R | 23.0 °C | 125 [-] Show Material materials with Hardness, Rockwell R of 125 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -6.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA |
23.0 °C | 13 kJ/m² Show Material materials with Impact strength, Charpy notched of 13 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 80 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 80 kJ/m² | ISO 179/1eU |
23.0 °C | 80 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 80 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | -30.0 °C | 60 kJ/m² Show Material materials with Impact strength, Izod notched of 60 kJ/m² | ISO 180/1U |
23.0 °C | 60 kJ/m² Show Material materials with Impact strength, Izod notched of 60 kJ/m² | ISO 180/1U | |
Impact strength, Izod unnotched | -40.0 °C | 10 kJ/m² Show Material materials with Impact strength, Izod unnotched of 10 kJ/m² | ISO 180/1A |
23.0 °C | 12 kJ/m² Show Material materials with Impact strength, Izod unnotched of 12 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 210 MPa Show Material materials with Tensile strength of 210 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.7E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.7E-5 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 8.5E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 8.5E-5 1/K | ISO 11359-1/-2 | ||
Glass transition temperature | 70 °C Show Material materials with Glass transition temperature of 70 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 260 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 260 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 252 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 252 °C | ISO 75-1/-2 | |||
Melting point | 263 °C Show Material materials with Melting point of 263 °C | ISO 11357-1/-3 | 18°F/min | |||
Specific heat capacity | 23.0 °C | 2130 J/(kg·K) Show Material materials with Specific heat capacity of 2130 J/(kg·K) | of melt | ||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, Burning Behav. at thickness h: HB class, Thickness tested: 0.7 mm, Oxygen index: 21 %, Glow Wire Flammability Index, 80mil: 650 °C, Glow Wire Flammability Index, 120mil: 750 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 30 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 1MHz | 23.0 °C | 4.1 [-] Show Material materials with Dielectric constant, 1MHz of 4.1 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 35% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |