General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.38 g/cm³ Show Material materials with Density of 1.38 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 4.8 GPa Show Material materials with Elastic modulus of 4.8 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 15 % Show Material materials with Elongation of 15 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 4.4 GPa Show Material materials with Flexural modulus of 4.4 GPa | ISO 178 |
Impact strength, Charpy notched | -40.0 °C | 4 kJ/m² Show Material materials with Impact strength, Charpy notched of 4 kJ/m² | ISO 179/1eA |
-6.0 °C | 5 kJ/m² Show Material materials with Impact strength, Charpy notched of 5 kJ/m² | ISO 179/1eA | |
23.0 °C | 7 kJ/m² Show Material materials with Impact strength, Charpy notched of 7 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 75 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 75 kJ/m² | ISO 179/1eU |
23.0 °C | 120 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 120 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | -30.0 °C | 85 kJ/m² Show Material materials with Impact strength, Izod notched of 85 kJ/m² | ISO 180/1U |
23.0 °C | 110 kJ/m² Show Material materials with Impact strength, Izod notched of 110 kJ/m² | ISO 180/1U | |
Impact strength, Izod unnotched | -40.0 °C | 5 kJ/m² Show Material materials with Impact strength, Izod unnotched of 5 kJ/m² | ISO 180/1A |
-30.0 °C | 6 kJ/m² Show Material materials with Impact strength, Izod unnotched of 6 kJ/m² | ISO 180/1A | |
23.0 °C | 7 kJ/m² Show Material materials with Impact strength, Izod unnotched of 7 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.36 [-] Show Material materials with Poisson's ratio of 0.36 [-] | |
Tensile strength | 23.0 °C | 78 MPa Show Material materials with Tensile strength of 78 MPa | ISO 527-1/-2 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 215 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 215 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 80 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 80 °C | ISO 75-1/-2 | |
Melting point | 257 °C Show Material materials with Melting point of 257 °C | ISO 11357-1/-3 | 18°F/min | |
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Technological properties
Property | ||
---|---|---|
Fillers | 32% Mineral Powder | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |