General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.06 g/cm³ Show Material materials with Density of 1.06 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.4 % Show Material materials with Water absorption of 0.4 % | Sim. to ISO 62 | Immersion 24h |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.4 GPa Show Material materials with Elastic modulus of 2.4 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 35 % Show Material materials with Elongation of 35 % | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 4.3 % Show Material materials with Elongation at yield of 4.3 % | ISO 527-1/-2 | ||
Flexural strength | 23.0 °C | 85 MPa Show Material materials with Flexural strength of 85 MPa | ISO 178 | ||
Hardness, Rockwell R | 23.0 °C | 114 [-] Show Material materials with Hardness, Rockwell R of 114 [-] | ISO 2039-2 | ||
Impact strength, Charpy notched | -6.0 °C | 4.2 kJ/m² Show Material materials with Impact strength, Charpy notched of 4.2 kJ/m² | ISO 179/1eA | ||
23.0 °C | 4.2 kJ/m² Show Material materials with Impact strength, Charpy notched of 4.2 kJ/m² | ISO 179/1eA | |||
Impact strength, Izod unnotched | -30.0 °C | 5 kJ/m² Show Material materials with Impact strength, Izod unnotched of 5 kJ/m² | ISO 180/1A | ||
23.0 °C | 4 kJ/m² Show Material materials with Impact strength, Izod unnotched of 4 kJ/m² | ISO 180/1A | |||
Poisson's ratio | 23.0 °C | 0.38 [-] Show Material materials with Poisson's ratio of 0.38 [-] | |||
Yield strength | 23.0 °C | 62 MPa Show Material materials with Yield strength of 62 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy unnotched | No Break @ 23,-6°C, ISO 179/1eA |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.2E-4 1/K Show Material materials with Coefficient of thermal expansion of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.2E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Glass transition temperature | 60 °C Show Material materials with Glass transition temperature of 60 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 135 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 135 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 62 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 62 °C | ISO 75-1/-2 | |||
Melting point | 218 °C Show Material materials with Melting point of 218 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 105 °C Show Material materials with Relative temperature index, electrical of 105 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 65 °C Show Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | 120mil | |||
Specific heat capacity | 23.0 °C | 2660 J/(kg·K) Show Material materials with Specific heat capacity of 2660 J/(kg·K) | of solid | ||
Thermal conductivity | 23.0 °C | 0.22 W/(m·K) Show Material materials with Thermal conductivity of 0.22 W/(m·K) | of solid | ||
Vicat softening temperature | 180 °C Show Material materials with Vicat softening temperature of 180 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.86 mm, UL recognition: yes -, Oxygen index: 25 %, Glow Wire Flammability Index, 15mil: 850 °C, Glow Wire Flammability Index, 30mil: 850 °C, Glow Wire Flammability Index, 40mil: 850 °C, Glow Wire Flammability Index, 60mil: 850 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 725 °C, Glow Wire Ignition Temperature, 15mil: 725 °C, Glow Wire Ignition Temperature, 40mil: 725 °C, Glow Wire Ignition Temperature, 60mil: 725 °C, Glow Wire Ignition Temperature, 80mil: 725 °C, Glow Wire Ignition Temperature, 120mil: 725 °C, Glow Wire Temperature, No Flame, 30mil: 700 °C, Glow Wire Temperature, No Flame, 40mil: 700 °C, Glow Wire Temperature, No Flame, 60mil: 700 °C, Glow Wire Temperature, No Flame, 80mil: 700 °C, Glow Wire Temperature, No Flame, 120mil: 700 °C, FMVSS Class: SE - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 100Hz | 23.0 °C | 3.6 [-] Show Material materials with Dielectric constant, 100Hz of 3.6 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 3.2 [-] Show Material materials with Dielectric constant, 1MHz of 3.2 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 36 kV/mm Show Material materials with Dielectric strength of 36 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 100Hz of 0.01 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.15%, Min. melt temperature: 230°C, Max. melt temperature: 290°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C |