Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.19 g/cm³ Show Material materials with Density of 1.19 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 4.2 GPa Show Material materials with Elastic modulus of 4.2 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 4 % Show Material materials with Elongation of 4 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 3.6 GPa Show Material materials with Flexural modulus of 3.6 GPa | ISO 178 |
Flexural strength | 23.0 °C | 140 MPa Show Material materials with Flexural strength of 140 MPa | ISO 178 |
Hardness, Rockwell M | 23.0 °C | 70 [-] Show Material materials with Hardness, Rockwell M of 70 [-] | ISO 2039-2 |
Hardness, Rockwell R | 23.0 °C | 110 [-] Show Material materials with Hardness, Rockwell R of 110 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -40.0 °C | 4 kJ/m² Show Material materials with Impact strength, Charpy notched of 4 kJ/m² | ISO 179/1eA |
-6.0 °C | 6 kJ/m² Show Material materials with Impact strength, Charpy notched of 6 kJ/m² | ISO 179/1eA | |
23.0 °C | 14 kJ/m² Show Material materials with Impact strength, Charpy notched of 14 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | 23.0 °C | 80 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 80 kJ/m² | ISO 179/1eU |
Impact strength, Izod notched | -30.0 °C | 90 kJ/m² Show Material materials with Impact strength, Izod notched of 90 kJ/m² | ISO 180/1U |
23.0 °C | 90 kJ/m² Show Material materials with Impact strength, Izod notched of 90 kJ/m² | ISO 180/1U | |
Impact strength, Izod unnotched | -40.0 °C | 7 kJ/m² Show Material materials with Impact strength, Izod unnotched of 7 kJ/m² | ISO 180/1A |
-30.0 °C | 10 kJ/m² Show Material materials with Impact strength, Izod unnotched of 10 kJ/m² | ISO 180/1A | |
23.0 °C | 13 kJ/m² Show Material materials with Impact strength, Izod unnotched of 13 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.36 [-] Show Material materials with Poisson's ratio of 0.36 [-] | |
Tensile strength | 23.0 °C | 85 MPa Show Material materials with Tensile strength of 85 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 4.6E-5 1/K Show Material materials with Coefficient of thermal expansion of 4.6E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.2E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.2E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Heat deflection temperature, 0.45 MPa | 246 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 246 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 220 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 220 °C | ISO 75-1/-2 | |||
Melting point | 263 °C Show Material materials with Melting point of 263 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 120 °C Show Material materials with Relative temperature index, electrical of 120 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 105 °C Show Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 105 °C Show Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | 120mil | |||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 580 V Show Material materials with Comparative tracking index of 580 V | IEC 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 14% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 80°C, Min. mold temperature: 50°C, Max. mold temperature: 100°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |