General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.28 g/cm³ Show Material materials with Density of 1.28 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 2.2 % Show Material materials with Water absorption of 2.2 % | Sim. to ISO 62 | Immersion 24h |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 8.2 GPa Show Material materials with Elastic modulus of 8.2 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 4 % Show Material materials with Elongation of 4 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 7.5 GPa Show Material materials with Flexural modulus of 7.5 GPa | ISO 178 |
Flexural strength | 23.0 °C | 220 MPa Show Material materials with Flexural strength of 220 MPa | ISO 178 |
Impact strength, Charpy notched | -40.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA |
-6.0 °C | 10 kJ/m² Show Material materials with Impact strength, Charpy notched of 10 kJ/m² | ISO 179/1eA | |
23.0 °C | 15 kJ/m² Show Material materials with Impact strength, Charpy notched of 15 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -40.0 °C | 80 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 80 kJ/m² | ISO 179/1eU |
-6.0 °C | 90 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 90 kJ/m² | ISO 179/1eU | |
23.0 °C | 85 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 85 kJ/m² | ISO 179/1eU | |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | |
Tensile strength | 23.0 °C | 160 MPa Show Material materials with Tensile strength of 160 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.7E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.7E-5 1/K | ISO 11359-1/-2 | 23 - 55°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 1.3E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.3E-4 1/K | ISO 11359-1/-2 | 55 - 160°C |
Heat deflection temperature, 1.80 MPa | 245 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 245 °C | ISO 75-1/-2 | |
Melting point | 260 °C Show Material materials with Melting point of 260 °C | ISO 11357-1/-3 | 18°F/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 25% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 80°C, Min. mold temperature: 50°C, Max. mold temperature: 100°C, Hold pressure time: 3s/mm |