Zytel® FGFE5171 NC010C

Alternative and trade names
PA66-GF33
Want to keep this datasheet? Save it now in your required format

Description

Zytel® FGFE5171 NC010C is a 33% glass filled nylon 66 resin. It has been developed for consideration into applications such as parts for the food industry.FOOD CONTACTThis product is manufactured according to Good Manufacturing Practice (GMP) principles and generally accepted in food contact applications in Europe and the USA when meeting applicable use conditions. For details, individual compliance statements are available from your DuPont representative.

Equivalent Materials

This material data has been provided by Matmatch.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValueComment

Density

23.0 °C

1.39 g/cm³

Show Material materials with Density of 1.39 g/cm³

ISO 1183

Mechanical

PropertyTemperatureValueComment

Elastic modulus

23.0 °C

10.5 GPa

Show Material materials with Elastic modulus of 10.5 GPa

ISO 527-1/-2

Elongation

23.0 °C

3.5 %

Show Material materials with Elongation of 3.5 %

ISO 527-1/-2

Flexural modulus

23.0 °C

9.3 GPa

Show Material materials with Flexural modulus of 9.3 GPa

ISO 178

Flexural strength

23.0 °C

290 MPa

Show Material materials with Flexural strength of 290 MPa

ISO 178

Impact strength, Charpy notched

23.0 °C

10 kJ/m²

Show Material materials with Impact strength, Charpy notched of 10 kJ/m²

ISO 179/1eA

Poisson's ratio

23.0 °C

0.34 [-]

Show Material materials with Poisson's ratio of 0.34 [-]

Tensile strength

23.0 °C

200 MPa

Show Material materials with Tensile strength of 200 MPa

ISO 527-1/-2

Thermal

PropertyValueComment

Heat deflection temperature, 1.80 MPa

252 °C

Show Material materials with Heat deflection temperature, 1.80 MPa of 252 °C

ISO 75-1/-2

Melting point

263 °C

Show Material materials with Melting point of 263 °C

ISO 11357-1/-3 | 18°F/min

Relative temperature index, electrical

130 °C

Show Material materials with Relative temperature index, electrical of 130 °C

UL 746B | 120mil

Relative temperature index, mechanical impact

120 °C

Show Material materials with Relative temperature index, mechanical impact of 120 °C

UL 746B | 120mil

Relative temperature index, mechanical strength

130 °C

Show Material materials with Relative temperature index, mechanical strength of 130 °C

UL 746B | 120mil

Flammability

Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.71 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min

Rheological Properties

PropertyTemperatureValueComment

Shrinkage

23.0 °C

0.3 %

Show Material materials with Shrinkage of 0.3 %

ISO 294-4, 2577

Shrinkage, transverse

23.0 °C

0.9 %

Show Material materials with Shrinkage, transverse of 0.9 %

ISO 294-4, 2577

Technological properties

Property
Fillers

33% Glass Fiber

Processing methods

Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C