General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.16 g/cm³ Show Material materials with Density of 1.16 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 1.8 % Show Material materials with Water absorption of 1.8 % | Sim. to ISO 62 | Immersion 24h |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 3.75 GPa Show Material materials with Elastic modulus of 3.75 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 10 % Show Material materials with Elongation of 10 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 3.66 GPa Show Material materials with Flexural modulus of 3.66 GPa | ISO 178 |
Impact strength, Charpy notched | -40.0 °C | 3 kJ/m² Show Material materials with Impact strength, Charpy notched of 3 kJ/m² | ISO 179/1eA |
-6.0 °C | 3 kJ/m² Show Material materials with Impact strength, Charpy notched of 3 kJ/m² | ISO 179/1eA | |
23.0 °C | 3.7 kJ/m² Show Material materials with Impact strength, Charpy notched of 3.7 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | 23.0 °C | 135 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 135 kJ/m² | ISO 179/1eU |
Poisson's ratio | 23.0 °C | 0.36 [-] Show Material materials with Poisson's ratio of 0.36 [-] | |
Tensile strength | 23.0 °C | 80 MPa Show Material materials with Tensile strength of 80 MPa | ISO 527-1/-2 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 235 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 235 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 84 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 84 °C | ISO 75-1/-2 | |
Melting point | 260 °C Show Material materials with Melting point of 260 °C | ISO 11357-1/-3 | 18°F/min | |
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 120mil | |
Relative temperature index, mechanical impact | 75 °C Show Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | 120mil | |
Relative temperature index, mechanical strength | 85 °C Show Material materials with Relative temperature index, mechanical strength of 85 °C | UL 746B | 120mil | |
Flammability | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 0.75 mm, UL recognition: yes -, Oxygen index: 39 %, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 60mil: 775 °C, Glow Wire Ignition Temperature, 120mil: 775 °C, FMVSS Class: DNI - |
Electrical
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 280°C, Min. melt temperature: 270°C, Max. melt temperature: 290°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |