Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.57 g/cm³ Show Material materials with Density of 1.57 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 3.6 % Show Material materials with Water absorption of 3.6 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 15 GPa Show Material materials with Elastic modulus of 15 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2.4 % Show Material materials with Elongation of 2.4 % | ISO 527-1/-2 |
Flexural modulus | 23.0 °C | 13 GPa Show Material materials with Flexural modulus of 13 GPa | ISO 178 |
Flexural strength | 23.0 °C | 330 MPa Show Material materials with Flexural strength of 330 MPa | ISO 178 |
Hardness, Rockwell M | 23.0 °C | 109 [-] Show Material materials with Hardness, Rockwell M of 109 [-] | ISO 2039-2 |
Hardness, Rockwell R | 23.0 °C | 125 [-] Show Material materials with Hardness, Rockwell R of 125 [-] | ISO 2039-2 |
Impact strength, Charpy notched | -40.0 °C | 13 kJ/m² Show Material materials with Impact strength, Charpy notched of 13 kJ/m² | ISO 179/1eA |
-6.0 °C | 12 kJ/m² Show Material materials with Impact strength, Charpy notched of 12 kJ/m² | ISO 179/1eA | |
23.0 °C | 12 kJ/m² Show Material materials with Impact strength, Charpy notched of 12 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 85 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 85 kJ/m² | ISO 179/1eU |
23.0 °C | 90 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 90 kJ/m² | ISO 179/1eU | |
Impact strength, Izod notched | 23.0 °C | 87 kJ/m² Show Material materials with Impact strength, Izod notched of 87 kJ/m² | ISO 180/1U |
Impact strength, Izod unnotched | -40.0 °C | 13 kJ/m² Show Material materials with Impact strength, Izod unnotched of 13 kJ/m² | ISO 180/1A |
23.0 °C | 12 kJ/m² Show Material materials with Impact strength, Izod unnotched of 12 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | |
Tensile strength | 23.0 °C | 240 MPa Show Material materials with Tensile strength of 240 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.3E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.3E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 5E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 5E-5 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Glass transition temperature | 135 °C Show Material materials with Glass transition temperature of 135 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 286 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 286 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 265 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 265 °C | ISO 75-1/-2 | |||
Melting point | 300 °C Show Material materials with Melting point of 300 °C | ISO 11357-1/-3 | first heat | |||
Relative temperature index, electrical | 150 °C Show Material materials with Relative temperature index, electrical of 150 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 150 °C Show Material materials with Relative temperature index, mechanical impact of 150 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 150 °C Show Material materials with Relative temperature index, mechanical strength of 150 °C | UL 746B | 120mil | |||
Specific heat capacity | 23.0 °C | 1610 J/(kg·K) Show Material materials with Specific heat capacity of 1610 J/(kg·K) | of melt | ||
Flammability | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.85 mm, UL recognition: yes -, Oxygen index: 24 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: 29 mm/min |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 600 V Show Material materials with Comparative tracking index of 600 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 4.2 [-] Show Material materials with Dielectric constant, 100Hz of 4.2 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 3.9 [-] Show Material materials with Dielectric constant, 1MHz of 3.9 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 35 kV/mm Show Material materials with Dielectric strength of 35 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 9E-3 [-] Show Material materials with Dissipation factor, 100Hz of 9E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 45% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 6-8h, Processing Moisture Content: ≤0.1%, Melt Temperature Optimum: 325°C, Min. melt temperature: 320°C, Max. melt temperature: 330°C, Mold Temperature Optimum: 150°C, Min. mold temperature: 140°C, Max. mold temperature: 180°C |