General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.62 g/cm³ Show Material materials with Density of 1.62 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 4 % Show Material materials with Water absorption of 4 % | Sim. to ISO 62 | 80mil |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 6.5 GPa Show Material materials with Elastic modulus of 6.5 GPa | ISO 527-1/-2 |
Elongation | 23.0 °C | 2 % Show Material materials with Elongation of 2 % | ISO 527-1/-2 |
Impact strength, Charpy notched | -6.0 °C | 2 kJ/m² Show Material materials with Impact strength, Charpy notched of 2 kJ/m² | ISO 179/1eA |
23.0 °C | 2.5 kJ/m² Show Material materials with Impact strength, Charpy notched of 2.5 kJ/m² | ISO 179/1eA | |
Impact strength, Charpy unnotched | -6.0 °C | 20 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 20 kJ/m² | ISO 179/1eU |
23.0 °C | 20 kJ/m² Show Material materials with Impact strength, Charpy unnotched of 20 kJ/m² | ISO 179/1eU | |
Impact strength, Izod unnotched | -30.0 °C | 2 kJ/m² Show Material materials with Impact strength, Izod unnotched of 2 kJ/m² | ISO 180/1A |
23.0 °C | 2 kJ/m² Show Material materials with Impact strength, Izod unnotched of 2 kJ/m² | ISO 180/1A | |
Poisson's ratio | 23.0 °C | 0.35 [-] Show Material materials with Poisson's ratio of 0.35 [-] | |
Tensile strength | 23.0 °C | 73 MPa Show Material materials with Tensile strength of 73 MPa | ISO 527-1/-2 |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 6.4E-5 1/K Show Material materials with Coefficient of thermal expansion of 6.4E-5 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 8.1E-5 1/K Show Material materials with Coefficient of thermal expansion, transverse of 8.1E-5 1/K | ISO 11359-1/-2 | ||
Heat deflection temperature, 0.45 MPa | 238 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 238 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 145 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 145 °C | ISO 75-1/-2 | |||
Melting point | 263 °C Show Material materials with Melting point of 263 °C | ISO 11357-1/-3 | 18°F/min | |||
Relative temperature index, electrical | 120 °C Show Material materials with Relative temperature index, electrical of 120 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 115 °C Show Material materials with Relative temperature index, mechanical impact of 115 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 115 °C Show Material materials with Relative temperature index, mechanical strength of 115 °C | UL 746B | 120mil | |||
Specific heat capacity | 23.0 °C | 1700 J/(kg·K) Show Material materials with Specific heat capacity of 1700 J/(kg·K) | of melt | ||
Vicat softening temperature | 235 °C Show Material materials with Vicat softening temperature of 235 °C | ISO 306 | 90°F/h, 11 lbf | |||
Flammability | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-2 class, Thickness tested: 0.75 mm, UL recognition: yes -, Burning Behav. 5V at thickness h: 5VA class, Thickness tested: 1.5 mm, UL recognition: yes -, Glow Wire Flammability Index, 30mil: 960 °C, Glow Wire Flammability Index, 40mil: 960 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 800 °C, Glow Wire Ignition Temperature, 40mil: 800 °C, Glow Wire Ignition Temperature, 60mil: 800 °C, Glow Wire Ignition Temperature, 120mil: 800 °C, FMVSS Class: DNI - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 325 V Show Material materials with Comparative tracking index of 325 V | IEC 60112 |
Dielectric constant, 100Hz | 23.0 °C | 4.1 [-] Show Material materials with Dielectric constant, 100Hz of 4.1 [-] | IEC 62631-2-1 |
Dielectric constant, 1MHz | 23.0 °C | 3.7 [-] Show Material materials with Dielectric constant, 1MHz of 3.7 [-] | IEC 62631-2-1 |
Dielectric strength | 23.0 °C | 40 kV/mm Show Material materials with Dielectric strength of 40 kV/mm | IEC 60243-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 100Hz of 0.01 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 30% Mineral Powder | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |