General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.05 g/cm³ Show Material materials with Density of 1.05 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 0.9 GPa Show Material materials with Elastic modulus of 0.9 GPa | ISO 527-1/-2 | ||
Elongation | 23.0 °C | 230 % Show Material materials with Elongation of 230 % | ISO 527-1/-2 | 50mm/min | ||
Elongation at yield | 23.0 °C | 29 % Show Material materials with Elongation at yield of 29 % | ISO 527-1/-2 | ||
Flexural modulus | 23.0 °C | 0.85 GPa Show Material materials with Flexural modulus of 0.85 GPa | ISO 178 | ||
Impact strength, Charpy notched | -40.0 °C | 12 kJ/m² Show Material materials with Impact strength, Charpy notched of 12 kJ/m² | ISO 179/1eA | ||
23.0 °C | 80 kJ/m² Show Material materials with Impact strength, Charpy notched of 80 kJ/m² | ISO 179/1eA | |||
Impact strength, Izod unnotched | -40.0 °C | 13 kJ/m² Show Material materials with Impact strength, Izod unnotched of 13 kJ/m² | ISO 180/1A | ||
23.0 °C | 65 kJ/m² Show Material materials with Impact strength, Izod unnotched of 65 kJ/m² | ISO 180/1A | |||
Poisson's ratio | 23.0 °C | 0.45 [-] Show Material materials with Poisson's ratio of 0.45 [-] | |||
Tensile strength | 23.0 °C | 44 MPa Show Material materials with Tensile strength of 44 MPa | ISO 527-1/-2 | 50mm/min | ||
Yield strength | 23.0 °C | 31 MPa Show Material materials with Yield strength of 31 MPa | ISO 527-1/-2 | ||
Impact strength, Charpy unnotched | No Break @ 23°C, ISO 179/1eU | ||||
Impact strength, Izod notched | No Break @ 23°C, ISO 179/1eU |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.3E-4 1/K Show Material materials with Coefficient of thermal expansion of 1.3E-4 1/K | ISO 11359-1/-2 | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.4E-4 1/K Show Material materials with Coefficient of thermal expansion, transverse of 1.4E-4 1/K | ISO 11359-1/-2 | ||
Glass transition temperature | 50 °C Show Material materials with Glass transition temperature of 50 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 1.80 MPa | 40 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 40 °C | ISO 75-1/-2 | |||
Melting point | 218 °C Show Material materials with Melting point of 218 °C | ISO 11357-1/-3 | 18°F/min | |||
Flammability | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 60°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 270°C, Min. melt temperature: 260°C, Max. melt temperature: 280°C, Max. screw tangential speed: 0.3m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm, Ejection temperature: 190°C |